EMS-Grivory Grivory® TSG-25/4 PA666-GF25
| Category | Polymer , Thermoplastic , Nylon , Nylon 6/66 , Nylon 66/6, 30% Glass Fiber Reinforced |
| Manufacturer | EMS-Grivory (EMS-CHEMIE) |
| Trade Name | Grivory® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | EMS-Grivory Grivory® TSG-25/4 PA666-GF25.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by EMS Grivory
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 |
| Water Absorption | 6.0 % | 6.0 % | ISO 62 |
| Moisture Absorption | 2.50 % | 2.50 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm | 0.0070 in/in | ISO 294-4, 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 90.0 MPa | 13100 psi | conditioned; ISO 527-1/-2 |
| 165 MPa | 23900 psi | dry; ISO 527-1/-2 | |
| Tensile Strength, Yield | 90.0 MPa | 13100 psi | conditioned; ISO 527-1/-2 |
| Elongation at Break | 4.0 % | 4.0 % | dry; ISO 527-1/-2 |
| 6.0 % | 6.0 % | conditioned; ISO 527-1/-2 | |
| Elongation at Yield | 4.0 % | 4.0 % | conditioned; ISO 527-1/-2 |
| Tensile Modulus | 5.60 GPa | 812 ksi | conditioned; ISO 527-1/-2 |
| 7.70 GPa | 1120 ksi | dry; ISO 527-1/-2 | |
| Charpy Impact Unnotched | 6.00 J/cm² | 28.6 ft-lb/in² | dry; ISO 179/1eU |
| 7.00 J/cm² | 33.3 ft-lb/in² | conditioned; ISO 179/1eU | |
| 5.00 J/cm² @Temperature 30.0 °C |
23.8 ft-lb/in² @Temperature 86.0 °F |
dry; ISO 179/1eU | |
| 5.00 J/cm² @Temperature 30.0 °C |
23.8 ft-lb/in² @Temperature 86.0 °F |
conditioned; ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 25.0 µm/m-°C | 13.9 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C | 44.4 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 260 °C | 500 °F | 10°C/min; ISO 11357-1/-3 |
| Maximum Service Temperature, Air | 90.0 - 110 °C | 194 - 230 °F | long term; EMS |
| 180 °C | 356 °F | short term; EMS | |
| Deflection Temperature at 1.8 MPa (264 psi) | 225 °C | 437 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB | HB | IEC 60695-11-10 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Automotive | Air intake sytems | |
| Powertrain and Chassis | ||
| Electricals & Electronics | Electrical appliances | |
| Electrical equipment | ||
| Form | Granules | |
| Industry & Consumer goods | Housewares | |
| Mechanical Engineering | ||
| Sports & Leisure | ||
| Tools & Accessories | ||
| Processing | Injection Molding |
Users viewing this material also viewed the following:
- Arlon 31580R020 0.020" (0.508 mm) Uncured Silicone Rubber on HDPE Carrier (discontinued **)
- Lanxess Pocan® KU 2-7018 000000 PBT
- LATI Latamid 66 VH G/30 PA 66, 30% Glass Fiber Reinforced, Heat Stabilized
- Sichuan Deyang Haton® hXGR41 Polyphenylene Sulfide
- Total PPC 7612 Polypropylene, Heterophasic Copolymer
- Zircar Refractory Composites RS-101 Refractory Sheet
- Eagle Brass 762 Nickel Silver 12%, Extra Spring
- ExxonMobil Santoprene® 121-50E500 Thermoplastic Elastomer
- DuPont Performance Polymers Neoprene GW M2 Polychloroprene Rubber
Copyright © lookpolymers.com All Rights Reserved