SABIC Innovative Plastics ULTEM HU2110 PEI

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name ULTEM
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics ULTEM HU2110 PEI.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
10% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food contact compliant.
Physical Properties Metric English Comments
Specific Gravity 1.34 g/cc
1.34 g/cc
ASTM D792
Density 1.42 g/cc
0.0513 lb/in³
ISO 1183
Moisture Absorption 0.500 %
0.500 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.90 %
0.90 %
ISO 62
Linear Mold Shrinkage, Flow 0.0020 - 0.0040 cm/cm

@Thickness 3.20 mm
 0.0020 - 0.0040 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 11.3 g/10 min

@Load 6.60 kg,
Temperature 337 °C
 11.3 g/10 min

@Load 14.6 lb,
Temperature 639 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 115 MPa
16700 psi
Type I, 5 mm/min; ASTM D638
165 MPa
23900 psi
5 mm/min; ISO 527
Tensile Strength, Yield 114 MPa
16500 psi
Type I, 5 mm/min; ASTM D638
165 MPa
23900 psi
5 mm/min; ISO 527
Elongation at Break 2.0 %
2.0 %
5 mm/min; ISO 527
3.0 %
3.0 %
Type I, 5 mm/min; ASTM D638
Elongation at Yield 2.0 %
2.0 %
5 mm/min; ISO 527
3.0 %
3.0 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 4.61 GPa
669 ksi
5 mm/min; ASTM D638
9.50 GPa
1380 ksi
1 mm/min; ISO 527
Flexural Yield Strength 225 MPa
32600 psi
1.3 mm/min, 50 mm span; ASTM D790
228 MPa
33100 psi
2 mm/min; ISO 178
Flexural Modulus 6.85 GPa
994 ksi
1.3 mm/min, 50 mm span; ASTM D790
6.89 GPa
999 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.480 J/cm
0.899 ft-lb/in
ASTM D256
0.640 J/cm

@Temperature -30.0 °C
 1.20 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
Izod Impact, Notched (ISO) 64.0 kJ/m²
30.5 ft-lb/in²
80*10*4; ISO 180/1A
70.0 kJ/m²

@Temperature -30.0 °C
 33.3 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
Charpy Impact, Notched 6.50 J/cm²
30.9 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 8.00 J

@Temperature 23.0 °C
 5.90 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 25.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 13.9 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
25.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 13.9 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 50.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 27.8 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
50.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 27.8 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 205 °C
401 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
207 °C

@Thickness 6.40 mm
 405 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Vicat Softening Point 213 °C
415 °F
Rate B/120; ISO 306
220 °C
428 °F
Rate B/50; ASTM D1525
220 °C
428 °F
Rate B/50; ISO 306
Glass Transition Temp, Tg 217 °C
423 °F