Polymer Resources PC-G40-[color]-1 Polycarbonate, 40% Glass Reinforced with Mold Release

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 40% Glass Filled
Manufacturer Polymer Resources, LTD
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polymer Resources PC-G40-[color]-1 Polycarbonate, 40% Glass Reinforced with Mold Release.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polycarbonate, 40% Glass Reinforced with Mold ReleaseProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
Physical Properties Metric English Comments
Specific Gravity 1.50 g/cc
1.50 g/cc
ASTM D792
Linear Mold Shrinkage 0.0010 - 0.0030 cm/cm
0.0010 - 0.0030 in/in
ASTM D955
Melt Flow 2.0 - 10 g/10 min

@Load 1.20 kg,
Temperature 300 °C
2.0 - 10 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 165 MPa
24000 psi
ASTM D638
Tensile Strength, Yield 165 MPa
24000 psi
ASTM D638
Flexural Strength 179 MPa
26000 psi
ASTM D790
Flexural Modulus 8.96 GPa
1300 ksi
ASTM D790
Izod Impact, Notched 0.801 J/cm

@Temperature 22.8 °C
1.50 ft-lb/in

@Temperature 73.0 °F
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 152 °C
305 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 146 °C
295 °F
ASTM D648
Flammability, UL94 V-1

@Thickness 1.59 mm
V-1

@Thickness 0.0626 in
V-0

@Thickness 3.17 mm
V-0

@Thickness 0.125 in
Processing Properties Metric English Comments
Rear Barrel Temperature 293 - 316 °C
560 - 600 °F
Middle Barrel Temperature 304 - 327 °C
580 - 620 °F
Front Barrel Temperature 316 - 338 °C
600 - 640 °F
Melt Temperature 302 - 329 °C
575 - 625 °F
Mold Temperature 82.2 - 116 °C
180 - 240 °F
Drying Temperature 118 - 124 °C
245 - 255 °F
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Descriptive Properties Value Comments
Vent 0.0005