BASF Ultradur B 4040 G10 BK5110 50% Glass Filled PBT

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 50% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultradur B
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultradur B 4040 G10 BK5110 50% Glass Filled PBT.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Injection-molding grades containing 50% of glass fibers, for industrial parts with excellent surface quality.Applications: External door handles in vehicles, visible sunroof frames, over door handles, toaster castings, external mirrors, rear screen wiper arms in vehicles and sunroof wind deflectors.
Physical Properties Metric English Comments
Density 1.73 g/cc
0.0625 lb/in³
ISO 1183
Water Absorption 0.40 %
0.40 %
DIN 53495/1L
Moisture Absorption at Equilibrium 0.12 %
0.12 %
23°C/50% R.H.
Viscosity Test 90 cm³/g
90 cm³/g
Viscosity number
Linear Mold Shrinkage, Flow 0.0010 cm/cm
0.0010 in/in
Sheet
0.0024 cm/cm
0.0024 in/in
60x60x2mm; ISO 294
Linear Mold Shrinkage, Transverse 0.0075 cm/cm
0.0075 in/in
Sheet
0.0077 cm/cm
0.0077 in/in
60x60x2mm; ISO 294
Melt Flow 10.4 g/10 min

@Load 2.16 kg,
Temperature 275 °C
10.4 g/10 min

@Load 4.76 lb,
Temperature 527 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 165 MPa
23900 psi
5mm/min; ISO 527-2
Elongation at Break 1.5 %
1.5 %
5mm/min; ISO 527-2
Modulus of Elasticity 18.7 GPa
2710 ksi
ISO 527-2
Charpy Impact Unnotched 5.20 J/cm²
24.7 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 1.00 J/cm²
4.76 ft-lb/in²
ISO 179/1eA
Dart Drop, Total Energy <= 5.00 J
<= 3.69 ft-lb
ISO 6603-1
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 2.00 - 3.00 µm/m-°C

@Temperature 23.0 - 80.0 °C
1.11 - 1.67 µin/in-°F

@Temperature 73.4 - 176 °F
DIN 53752
Specific Heat Capacity 1.60 J/g-°C
0.382 BTU/lb-°F
IEC 1006
Melting Point 220 - 250 °C
428 - 482 °F
Maximum Service Temperature, Air 140 °C
284 °F
at 50% loss of tensile strength after 20000h; IEC 216-1
160 °C
320 °F
at 50% loss of tensile strength after 5000h; IEC 216-1
210 °C
410 °F
Deflection Temperature at 0.46 MPa (66 psi) 221 °C
430 °F
ISO 75-2
Deflection Temperature at 1.8 MPa (264 psi) 205 °C
401 °F
ISO 75-2
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
HB

@Thickness 0.800 mm
HB

@Thickness 0.0315 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+16 ohm
>= 1.00e+16 ohm
IEC 60093
Dielectric Constant 4.5

@Frequency 1.00e+6 Hz
4.5

@Frequency 1.00e+6 Hz
IEC 60250
4.7

@Frequency 100 Hz
4.7

@Frequency 100 Hz
IEC 60250
Dielectric Strength 16.0 kV/mm
406 kV/in
IEC 243/1
Dissipation Factor 0.015

@Frequency 1.00e+6 Hz
0.015

@Frequency 1.00e+6 Hz
IEC 60250
0.020

@Frequency 100 Hz
0.020

@Frequency 100 Hz
IEC 60250
Comparative Tracking Index 225 V
225 V
Test solution A; IEC 112
Processing Properties Metric English Comments
Melt Temperature 250 - 275 °C
482 - 527 °F
Injection molding
270 °C
518 °F
for shrinkage test
Mold Temperature 60.0 - 100 °C
140 - 212 °F
80.0 °C
176 °F
for shrinkage test
Descriptive Properties Value Comments
Color BK5110 and Colored
Commercial Status Active America
Form Pellets
Impact Modified No
Primary Processing Technique Injection Molding
Processing Injection Molding
Special characteristic Release agent