SABIC Innovative Plastics LNP Lubricomp EL004 PEI
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Lubricomp EL004 PEI.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubricomp* EL004 is a compound based on Polyetherimide resin containing PTFE. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | ASTM D 792 |
| 1.38 g/cc | 0.0499 lb/in³ | ISO 1183 | |
| Moisture Absorption at Equilibrium | 0.20 % @Time 86400 sec |
0.20 % @Time 24.0 hour |
50% RH; ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.0095 cm/cm @Time 86400 sec |
0.0095 in/in @Time 24.0 hour |
ISO 294 |
| 0.0090 - 0.011 cm/cm @Time 86400 sec |
0.0090 - 0.011 in/in @Time 24.0 hour |
ASTM D 955 | |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.012 cm/cm @Time 86400 sec |
0.010 - 0.012 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.011 cm/cm @Time 86400 sec |
0.011 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 72.0 MPa | 10400 psi | ISO 527 |
| 73.0 MPa | 10600 psi | ASTM D 638 | |
| Tensile Strength, Yield | 73.0 MPa | 10600 psi | ASTM D 638 |
| 73.0 MPa | 10600 psi | ISO 527 | |
| Elongation at Break | 7.6 % | 7.6 % | ASTM D 638 |
| 8.8 % | 8.8 % | ISO 527 | |
| Elongation at Yield | 6.3 % | 6.3 % | ASTM D 638 |
| 6.4 % | 6.4 % | ISO 527 | |
| Tensile Modulus | 2.60 GPa | 377 ksi | 1 mm/min; ISO 527 |
| 2.75 GPa | 399 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 96.0 MPa | 13900 psi | ISO 178 |
| Flexural Modulus | 2.06 GPa | 299 ksi | ASTM D 790 |
| 2.40 GPa | 348 ksi | ISO 178 | |
| Izod Impact, Notched | 0.530 J/cm @Temperature 23.0 °C |
0.993 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 5.39 J/cm @Temperature 23.0 °C |
10.1 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 36.0 kJ/m² @Temperature 23.0 °C |
17.1 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| 7.00 J @Temperature 23.0 °C |
5.16 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 | |
| Coefficient of Friction, Dynamic | 0.28 | 0.28 | ASTM D 3702 Modified |
| Coefficient of Friction, Static | 0.18 | 0.18 | ASTM D 3702 Modified |
| K (wear) Factor | 94.7 x 10-8 mm³/N-M | 47.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D 3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 48.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
27.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 49.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
27.2 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 50.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
27.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 50.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
28.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 203 °C | 397 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 206 °C @Thickness 3.20 mm |
403 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 187 °C | 369 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 187 °C @Thickness 3.20 mm |
369 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- Orion Engineered Carbons CORAX® N 330 ASTM Carbon Black
- Chevron Phillips KN 230B LDPE Injection Molding Resin (discontinued **)
- MarkeTech Silica Aerogel
- Solvay Specialty Polymers Catalyst CAT 10 Polyolefin
- Solvay Specialty Polymers Ryton® QC160N Polyphenylene Sulfide (PPS)
- Unifrax Foamfrax® Isofoam Fiber Insulation
- Plenco 4548 Phenolic, Granular, Transfer Molded
- DuPont Performance Polymers Zytel® HTN 54G35HSLR NC010 Polyphthalamide (PPA) (Unverified Data**)
- A. Schulman PP 2407 Polypropylene Impact Resistant Copolymer Polypropylene
- Pyrotek MT-29B Microporous Insulating Board
Copyright © lookpolymers.com All Rights Reserved