- Teijin Multilon TN-7000F Filler Reinforced Type, Halogen-Free Flame Resistant PC/ABS Polymer Alloy
Teijin Multilon TN-7000F Filler Reinforced Type, Halogen-Free Flame Resistant PC/ABS Polymer Alloy
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate (PC) |
| Manufacturer | Teijin |
| Trade Name | Multilon |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Teijin Multilon TN-7000F Filler Reinforced Type, Halogen-Free Flame Resistant PC/ABS Polymer Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Halogen-free flame retardant PC/ABS polymer alloy, and is also antimony-free. High stiffness realizes the thin wall of business machine chassis.Information provided by Teijin Chemicals Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm @Thickness 4.00 mm |
0.0040 - 0.0060 in/in @Thickness 0.157 in |
|
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm @Thickness 4.00 mm |
0.0040 - 0.0060 in/in @Thickness 0.157 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 46.0 MPa | 6670 psi | 50mm/min; ISO 527 |
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | 50mm/min; ISO 527 |
| Elongation at Break | 20 % | 20 % | 50mm/min; ISO 527 |
| Elongation at Yield | 2.0 % | 2.0 % | 50mm/min; ISO 527 |
| Tensile Modulus | 3.30 GPa | 479 ksi | 1mm/min; ISO 527 |
| Flexural Strength | 96.0 MPa | 13900 psi | 2mm/min; ISO 178 |
| Flexural Modulus | 3.20 GPa | 464 ksi | 2mm/min; ISO 178 |
| Charpy Impact Unnotched | NB | NB | ISO 179 |
| Charpy Impact, Notched | 1.20 J/cm² | 5.71 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 60.0 µm/m-°C @Temperature 20.0 °C |
33.3 µin/in-°F @Temperature 68.0 °F |
ISO 11359 |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C @Temperature 20.0 °C |
38.9 µin/in-°F @Temperature 68.0 °F |
ISO 11359 |
| Deflection Temperature at 0.46 MPa (66 psi) | 94.0 °C | 201 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C | 183 °F | ISO 75 |
| Vicat Softening Point | 97.0 °C | 207 °F | 50°C/hr, 50N; ISO 306 |
| Flammability, UL94 | V-0 @Thickness 1.20 mm |
V-0 @Thickness 0.0472 in |
|
| 5VB @Thickness 1.80 mm |
5VB @Thickness 0.0709 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | IEC 60093 |
Users viewing this material also viewed the following:
- Polymer Resources NY66-G50 Nylon 66, 50% Glass Reinforced
- REXtac Rextac® RT 1320 Amorphous Polyalphaolefin (APAO)
- Lehmann & Voss LUVOCOM® 1106-8133 Polyether imide, with carbon fiber, easy flowing
- Global EPP PA 612 Copolymer Cast Polyamide 612
- LyondellBasell Astryn NXO-21001 Polypropylene Copolymer
- A. Schulman PP 3353-01 Polypropylene Medium Impact Polypropylene
- A. Schulman POLYAXIS® LP624 Stabilized High Density Polyethylene
- A. Schulman POLYBATCH™ ASP-2000 Permanent Antistatic Product
- Denka REOMER G G3010 Thermoplastic Elastomer, For Extrusion
Copyright © lookpolymers.com All Rights Reserved