- Owens Corning Glass Fiber Reinforced Polycarbonate, 10 wt.% glass
Owens Corning Glass Fiber Reinforced Polycarbonate, 10 wt.% glass
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 10% Glass Filled |
| Manufacturer | Owens Corning |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Owens Corning Glass Fiber Reinforced Polycarbonate, 10 wt.% glass.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by the manufacturer, Owens Corning.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.26 g/cc | 0.0455 lb/in³ | ASTM D792 |
| Water Absorption | 0.14 % | 0.14 % | 24 hrs.; ASTM D570 |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 80 | 80 | ASTM D785 |
| Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | ASTM D638 |
| Elongation at Break | 9.0 % | 9.0 % | ASTM D638 |
| Modulus of Elasticity | 5.20 GPa | 754 ksi | ASTM D638 |
| Flexural Strength | 110 MPa | 16000 psi | ASTM D790 |
| Flexural Modulus | 4.00 GPa | 580 ksi | ASTM D790 |
| Compressive Strength | 97.0 MPa | 14100 psi | ASTM D695 |
| Izod Impact, Notched | 1.00 J/cm | 1.87 ft-lb/in |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 3.24 µm/m-°C @Temperature 20.0 °C |
1.80 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Specific Heat Capacity | 1.21 J/g-°C | 0.290 BTU/lb-°F | |
| Thermal Conductivity | 0.663 W/m-K | 4.60 BTU-in/hr-ft²-°F | ASTM C177 |
| Deflection Temperature at 1.8 MPa (264 psi) | 141 °C | 285 °F | ASTM D648 |
| Flammability, UL94 | V-1 | V-1 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.1 @Frequency 60 Hz |
3.1 @Frequency 60 Hz |
ASTM D150 |
| Dielectric Strength | 19.7 kV/mm | 500 kV/in | ASTM D149 |
| Arc Resistance | 125 sec | 125 sec | ASTM D495 |
Users viewing this material also viewed the following:
- LyondellBasell Hostacomâ„¢ 62F4-2C Polypropylene Homopolymer
- SPS Guang Zhou POLOYâ„¢ 2001(+) PC/ABS
- EMS-Griltech Griltex® D 1533E Copolyester Hotmelt Adhesive (Technical Applications)
- Dow Corning SILASTIC® LC-60-2004 PART A&B KIT
- DSM Arnite® AV2 370 HF PET-GF35
- Cytec EN-2551 (Conap) Potting and Encapsulation Adhesive
- Dow Corning 3-4133 DIELECTRIC GEL KIT
- 3M 2110 Polyethylene Protective Tapes
- BASF Ultramid® 1503-2 NF2004 33% Glass Filled PA66 (Conditioned)
Copyright © lookpolymers.com All Rights Reserved