Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 60.0 MPa | 8700 psi | |
Poco Graphite PLS Semiconductor Grade Graphite Although it is impossible to identify differences between various grades of graphite by looking at them, each grade has a special set of characteristics and physical properties that determine their .. |
|||
Flexural Strength | <= 60.0 MPa | <= 8700 psi | ISO 178 |
Polykemi AB POLYblend 6005B UV PC/ABS-Blend Information provided by Polykemi AB |
|||
Flexural Strength | 60.0 MPa | 8700 psi | ISO 178 |
Nilit FRIANYL A63 S15 Nylon 6.6 for injection molding Nylon 6.6 for injection molding, impact modified.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Flexural Strength | 60.0 MPa | 8700 psi | Longitudinal |
Quadrant Plastic Composites MultiQ® Impact Thermoplastic Panel Composite MultiQ is a product line of thermoplastic composites in panel form whose specific properties make them particularly suitable as an environmental alternative to plywood in outdoor applications. Howev.. |
|||
Flexural Strength | 60.0 - 80.0 MPa | 8700 - 11600 psi | Injection; ISO 178 |
Raschig Group 4552 Silicone Glass fiber reinforced silicone molding compound. Excellent thermal stability - up to +/- 300°C continuously, excellent electrical properties, good mechanical strength, very good dimensional stabi.. |
|||
Flexural Strength | 60.0 - 90.0 MPa | 8700 - 13100 psi | Compression; ISO 178 |
Raschig Group AMPLA® 2000 melamine-modified polyester Halogen-free, organically and inorganically filled melamine-modified Polyester molding compound. Low post-shrinkage, very good electrical values, high heat resistance, very good sliding behavior, ve.. |
|||
Flexural Strength | 60.0 MPa | 8700 psi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP FARADEX AS004 ABS (Europe-Africa-Middle East) LNP* Faradex* AS004 is a compound based on Acrylonitrile Butadiene Styrene resin containing Stainless Steel Fiber. Added features of this material include: EMI/RFI Shielding. |
|||
Flexural Strength | 60.0 MPa | 8700 psi | |
Plastcom SLOVAMID 6 MI/2 PA6, improved strength FeaturesPA 6 with the content of thermoplastic kaoutchouc. Impacted, for mouldings with high toughness either at minus temperatures, suitable for external use, eg. ski shoes, sports and safety helme.. |
|||
Flexural Strength | 60.0 MPa | 8700 psi | |
Lehmann & Voss LUVOCOM® 80-8268 Polyacetal-copolymer, with PTFE, lubricant modified Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Emergency running property, gl.. |
|||
Flexural Strength | 60.0 MPa | 8700 psi | after 16 hours in 50°C water |
Malvern Minerals Thermoplastic Polyester with Novacite® 1250 Quartz Filler Product data demonstrates the effect of the Novacite (untreated lamellar quartz) filler. A separate entry demonstrates the effect of surface-treated Novakup filler in thermoplastic polyester Th.. |
|||
Flexural Strength | 60.0 MPa | 8700 psi | 5 mm/min; ISO 178 |
Gromax BTE70-FN001N1 Nylon 6 (Dry) Information provided by Gromax Enterprises Corp. |
|||
Flexural Strength | 60.0 MPa | 8700 psi | ISO 178 |
Fiberfil® J-60/15/MI/20 Polypropylene Homopolymer, 35% Glass/mica Reinforced Information provided by FIBERFIL Engineered Plastics |
|||
Flexural Strength | 60.0 MPa | 8700 psi | DIN 54352 |
Schwartz Technical Plastics LAMIGAMID® 310 Cast Polyamide 6, Conditioned Application: sheaves, wheels, rollers, mandrell segments, coupling parts, vibrator parts etc.Information provided by Schwartz Technical Plastics GmbH |
|||
Flexural Strength | 60.0 MPa | 8700 psi | DIN 54352 |
Schwartz Technical Plastics LAMIGAMID® 319 Cast Polyamide 6, Oil Filled, Conditioned Application: sheaves and wheels without additional bearings, sliding linersInformation provided by Schwartz Technical Plastics GmbH |
|||
Flexural Strength | 60.0 MPa | 8700 psi | ISO 178 |
Styrolution Luran® S 796 M Colored ASA Description: High-impact injection molding gr4ade with good flowability.Applications: Trim panels for goods vehicles.Information provided by STYROLUTION, which is a joint venture between BASF and IN.. |
|||
Flexural Strength | 60.0 MPa | 8700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP SH0700B PA12 LNP* Thermocomp* SH0700B is a compound based on Nylon 12 containing proprietary fillers. Added feature: High Specific Gravity |
|||
Flexural Strength | 60.0 MPa | 8700 psi | ISO 178 |
Unitika A1025NO PA6, Flame Retardant, Conditioned Information provided by Unitika Ltd. |
|||
Flexural Strength | 60.0 MPa | 8700 psi | ISO 178-93 |
Wellman Wellamid® XT1482-BK High Impact Nylon 66 Description: High Impact Nylon 66Information provided by Wellman. |
|||
Flexural Strength | 60.0 MPa | 8700 psi | ISO 178-93 |
Wellman Wellamid® XT1627-WBK2 High Impact, Weatherable Nylon 66 Description: High Impact, Weatherable Nylon 66Information provided by Wellman. |
|||
Flexural Strength | 60.0 MPa | 8700 psi | ASTM D790 |
Plenco 6310 Phenolic, Granular, Compression Molded PLENCO 06310 is a glass and mineral filled phenolic molding compound offering excellent heat resistance and dimensional stability. 06310 is available in black.Information supplied by Plenco. |
|||
Flexural Strength | 60.0 MPa | 8700 psi | cond; ISO 178 |
DSM Novamid® 1010GN7-20 BK37 PA6-GF20 FR(30) 0 20% Glass Reinforced, Flame Retardant, Halogen free |
|||
Flexural Strength | 60.0 MPa | 8700 psi | ASTM D790 |
Aclo Accutech Polypropylene Copolymer CP0437G25M5CL Glass/Mineral Reinforced Coupled |
|||
Flexural Strength | 60.0 MPa | 8700 psi | ISO 178 |
Azoty Tarnow™ TARNOFORM 300 SI POM Tribological modified grade with silicon, for better sliding properties in plastic-plastic contact.Information provided by Zakłady Azotowe w Tarnowie-Moscicach S.A. |
|||
Flexural Strength | 60.0 - 80.0 MPa | 8700 - 11600 psi | |
Alliance BIN-40 Bonded (Composite) Magnetic Material |
|||
Flexural Strength | 60.0 MPa | 8700 psi | ASTM D790 |
Aclo Accutech Polypropylene Copolymer CP0436G20CL Glass Reinforced |
|||
Flexural Strength | 60.0 MPa | 8700 psi | 23°C, 50% RH; ASTM D790 |
Asahi Kasei Xyron® X0715 Modified Polyphenylene Ether AutomotiveInformation provided by Asahi Kasei |
|||
Flexural Strength | 60.0 MPa | 8700 psi | ISO 178 |
SABIC Innovative Plastics LNP Lubricomp CI001 PS (Asia Pacific) LNP* Lubricomp* CI001 is a compound based on Polystyrene resin containing Silicone. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for the Asia Pa.. |
|||
Flexural Strength | 60.0 MPa | 8700 psi | ISO 178 |
Polyram RamTal PM340S6 Polyacetal for Injection Molding, 30% Glass-Beads Filled 30% Glass-beads filled polyacetal for injection molding applications.Information provided by Polyram. |