Polykemi AB POLYblend 6005B UV PC/ABS-Blend
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Polykemi AB |
| Trade Name | POLYblend |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB POLYblend 6005B UV PC/ABS-Blend.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0080 - 0.010 cm/cm | 0.0080 - 0.010 in/in | With Flow; ISO 2577 |
| 0.0080 - 0.010 cm/cm | 0.0080 - 0.010 in/in | Across Flow; ISO 2577 | |
| Melt Index of Compound | 14 g/10 min @Load 5.00 kg, Temperature 240 °C |
14 g/10 min @Load 11.0 lb, Temperature 464 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 62 @Time 15.0 sec |
62 @Time 0.00417 hour |
ASTM D2240 |
| Tensile Strength at Break | <= 45.0 MPa | <= 6530 psi | ISO/R527 |
| Elongation at Break | >= 80 % | >= 80 % | ISO/R527 |
| Flexural Strength | <= 60.0 MPa | <= 8700 psi | ISO 178 |
| Flexural Modulus | 1.80 GPa @Temperature 23.0 °C |
261 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact, Notched | 5.00 J/cm² @Temperature 23.0 °C |
23.8 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 96.0 °C | 205 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | 110 °C @Load 5.001 kg |
230 °F @Load 11.03 lb |
50°C/h; ISO 306 |
| 190 °C @Load 1.00 kg |
374 °F @Load 2.21 lb |
50°C/h; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| Glow Wire Test | 650 °C @Thickness 2.00 mm |
1200 °F @Thickness 0.0787 in |
IEC 695-2-1 |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPE RP 6568 CT BLK
- Polykemi AB SCANAMID 66 A12^ F30 TF15 Nylon 66, Glass Fiber Reinforced, Modified
- Chevron Phillips HiD® 9075 HDPE Injection Molding Resin (discontinued **)
- Lehmann & Voss LUVOCOM® 1105-8002 PEEK, with carbon fiber
- Global PP-2340-S Polypropylene Block Copolymer
- LATI Larpeek 10 K/30 PEEK, 30% Carbon Fiber Reinforced
- Solvay TECHNYL® C 548B V15 Black PA6, 15% glass filled, DRY
- Daikin DAI-EL G-716 Fluoroelastomer Copolymer, Bisphenol Curable Grade, 66% Fluorine Content
- Braskem GP100BK HDPE High Density Extrusion Polyethylene
Copyright © lookpolymers.com All Rights Reserved