Schwartz Technical Plastics LAMIGAMID® 319 Cast Polyamide 6, Oil Filled, Conditioned
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Cast |
| Manufacturer | Schwartz Technical Plastics |
| Trade Name | LAMIGAMID® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Schwartz Technical Plastics LAMIGAMID® 319 Cast Polyamide 6, Oil Filled, Conditioned.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Application: sheaves and wheels without additional bearings, sliding linersInformation provided by Schwartz Technical Plastics GmbH
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ISO R 1183 |
| Moisture Absorption at Equilibrium | 1.0 % | 1.0 % | DIN 53473 |
| Water Absorption at Saturation | 4.0 % @Temperature 20.0 °C |
4.0 % @Temperature 68.0 °F |
ISO R 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 130 MPa | 18900 psi | Hc 30; ISO 2039; partially |
| Tensile Strength, Yield | 70.0 MPa | 10200 psi | ISO-DIS 527 |
| Creep Strength | >= 12.0 MPa | >= 1740 psi | 1% elongation, 1000 h; DIN 53444 |
| >= 16.0 MPa | >= 2320 psi | 2% elongation, 1000 h; DIN 53444 | |
| Tensile Modulus | 2.80 GPa | 406 ksi | DIN 53457 |
| Flexural Strength | 60.0 MPa | 8700 psi | DIN 54352 |
| Flexural Modulus | 2.50 GPa | 363 ksi | DIN 53457 |
| Compressive Strength | 21.0 MPa | 3050 psi | 5% pressing; EN ISO 604 |
| 43.0 MPa | 6240 psi | 10% pressing; EN ISO 604 | |
| 66.0 MPa | 9570 psi | 20% pressing; EN ISO 604 | |
| Izod Impact, Notched (ISO) | >= 15.0 kJ/m² | >= 7.14 ft-lb/in² | ISO 180-1A |
| Izod Impact Resistance | NB | NB | swinging hammer 0,1 DIN 51222; DIN 53453 |
| Coefficient of Friction | 0.080 | 0.080 | With lubrication |
| Coefficient of Friction, Dynamic | 0.20 | 0.20 | no lube; Steel 2162, Rvst=2E-6m, p=0.05 Mpa, v=0.6 m/s, t=40°C |
| Tear Strength Test | >= 0.25 | >= 0.25 | ISO-DIS 527 |
| K Factor (Wear Factor) | 4.0e-11 | 4.0e-11 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 70.0 - 80.0 µm/m-°C @Temperature 20.0 - 100 °C |
38.9 - 44.4 µin/in-°F @Temperature 68.0 - 212 °F |
DIN 53752 |
| Specific Heat Capacity | 1.67 J/g-°C | 0.399 BTU/lb-°F | |
| Thermal Conductivity | 0.250 W/m-K | 1.74 BTU-in/hr-ft²-°F | DIN 52612 |
| Melting Point | 220 °C | 428 °F | ISO R 1218 |
| Maximum Service Temperature, Air | 120 °C | 248 °F | Continuous |
| 180 °C | 356 °F | Intermittent | |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | V-notch; ISO R 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | V-notch; ISO R 75 |
| Minimum Service Temperature, Air | -40.0 °C | -40.0 °F | Continuous |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | DIN 53482 |
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | DIN 53482 |
| Dielectric Constant | 3.7 | 3.7 | DIN 53483 |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | DIN 53481 |
| Dielectric Loss Index | 0.030 | 0.030 | DIN 53483 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Creepage/leakage Resistance | KA3b | DIN 53480 |
Users viewing this material also viewed the following:
- Stellarchem SV-B75E TPV Compound
- Master Bond EP45HT-1 Adhesive Resists Exposure to Sterilization
- Tipco Tipcolite® TMS 211 Phenolic Compound, Cotton, Filler & Wood Flour, having Medium Flow & High Strength
- Total Lumicene® mPE M 2710 EP Metallocene Polyethylene, Film
- A. Schulman POLYFORT™ FXP 2600-3120 CaC02 Filled Homopolymer Polypropylene
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, Hardness 70A, Non-Black Sulfur Cure
- Eurotec® Tecopet® PT70 GR15 NL100 MB PET, 15% glass fiber reinforced, impact modified, heat stabilized, natural
- Ametek Molybdenum-Copper Composite AMC 6436
- A. Schulman POLYBATCH™ Grey LL80316/3 Concentrate Based In LLDPE
Copyright © lookpolymers.com All Rights Reserved