SABIC Innovative Plastics LNP THERMOCOMP SH0700B PA12
| Category | Polymer , Thermoplastic , Nylon , Nylon 12 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP SH0700B PA12.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* SH0700B is a compound based on Nylon 12 containing proprietary fillers. Added feature: High Specific Gravity
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 6.90 g/cc | 0.249 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 40.0 MPa | 5800 psi | Type I, 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 41.0 MPa | 5950 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 1.8 % | 1.8 % | Type I, 5 mm/min; ASTM D638 |
| Elongation at Yield | 1.6 % | 1.6 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 5.22 GPa | 757 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 60.0 MPa | 8700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 4.46 GPa | 647 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 0.660 J/cm | 1.24 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.36 J/cm | 6.29 ft-lb/in | ASTM D4812 |
Users viewing this material also viewed the following:
- NYCOA 2046 Copolymer Nylon 6/69
- Nylene® 453 Nylon 6
- Gouda Vuurvast A 1 S Dense Refractory Brick
- Seals Eastern 5724 Fluorocarbon-Elastomer
- SABIC Innovative Plastics Xylex X7200MR PC+POLYESTER (Asia Pacific)
- China-Yixing Longly Refractories Seggar Semi-Corundum-Mullite
- ExxonMobil Mobil Pegasus 801 40
- Aclo Accutech Polypropylene Homopolymer HP0334T10L Talc Reinforced
- Solvay SOPROPHOR® TS/54 Surfactant
Copyright © lookpolymers.com All Rights Reserved