Polymer Property : Flexural Strength = 19900 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	137 MPa	19900 psi	ISO 178
SABIC Innovative Plastics LNP KONDUIT OTF2B PPS - Linear LNP KONDUIT* OTF2B is a compound based on PPS - Linear resin containing 10% Glass Fiber, 55% Proprietary Thermal Filler. Added features of this material include: Thermally Conductive.
Flexural Strength	137 MPa	19900 psi	ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP DFL36G PC LNP* Lubricomp* DFL36G is a compound based on Polycarbonate resin containing 30% Mixed Glass, 15% PTFE. Added features of this material include: Internally Lubricated.
Flexural Strength	137 MPa	19900 psi	ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP DFL23 PC LNP* Lubricomp* DFL23 is a compound based on Polycarbonate resin containing 15% Glass Fiber and 10% PTFE. Added features include: Internally Lubricated.
Flexural Strength	137 MPa	19900 psi	ASTM D790
Mitsui AURUM® 450 Thermoplastic Polyimide Resin, Non-filled (discontinued **) AURUM® is an easy melt, processable and recyclable thermoplastic polyimide resin that provides continuous service temperatures to 465° F in its amorphous state and up to 550° F when annealed to i..
Flexural Strength	137 MPa	19900 psi	ASTM D790
LG Chemical EG920 PMMA, General Purpose Grade for Extrusion General purpose grade with excellent stress cracking resistanceIntended mainly for exterior applicationsRecommended mainly for sheets, pipes, and profilesFeatures: Excellent transparency and eleganc..
Flexural Strength	137 MPa	19900 psi	ASTM D790
LG Chemical IG840 PMMA, General Purpose Grade for Injection Molding General purpose grade with better flowability than IH 830 but slightly below in heat resistanceMechanical strength and surface hardnessFeatures: Excellent transparency and eleganceWeather resistance..
Flexural Strength	137 MPa	19900 psi	ASTM D790
LG Chemical LUCEL CF-610 Electrically Conductive POM, 10% Carbon Fiber Filled, High Strength, Wear Resistant LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m..
Flexural Strength	137 MPa	19900 psi	ASTM D790
LG Chemical LUCON PO-5300H Electrically Conductive Thermoplastic LG Chemicals has formulated a diverse range of LUCON thermoplastic compounds containing conductive additives, such as carbon powder, (nickel coated) carbon fiber, or stainless steel fiber for solvin..
Flexural Strength	137 MPa	19900 psi	ASTM D790
LG Chemical LUPOY GP-5200 General Purpose PC/ABS Alloy, 10% Polymer Alloy, High Strength Among the characteristics of LUPOY polycarbonate resins are excellent mechanical properties, high heat resistance, high impact strength, and dimensional stability.Applications:Automotive: Automotive..
Flexural Strength	137 MPa	19900 psi	ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP RA004 PA 66 (Asia Pacific) LNP LUBRICOMP* RA004 is a compound based on Nylon 66 resin containing Aramid. Added features of this material include: Internally Lubricated.
Flexural Strength	137 MPa	19900 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ValoxÂ® 4521 PBT VALOX 4521 is a high flow, 20% glass reinforced flame retardant PBT injection moulding resin. Applications: electrical applications
Flexural Strength	137 MPa	19900 psi	ISO 178
SABIC Innovative Plastics LNP Stat-kon DEP32XXC PC LNP STAT-KON* DEP32XXC is a compound based on Polycarbonate resin containing Carbon Fiber, Silicone, PTFE. Added features of this material include: Electrically Conductive.This data was supplied by..
Flexural Strength	137 MPa	19900 psi	ASTM D 790
SABIC Innovative Plastics LNP Thermocomp 5C004 LNP* Thermocomp* 5C004 is a compound based on Polyvinylidene Fluoride resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.This data was supplied by SABIC..
Flexural Strength	137 MPa	19900 psi	ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP 5C004 PVDF (Asia Pacific) LNP* Thermocomp* 5C004 is a compound based on Polyvinylidene Fluoride resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.
Flexural Strength	137 MPa	19900 psi	ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP GF004 PSU LNP* Thermocomp* GF004 is a compound based on Polysulfone resin containing 20% Glass Fiber.
Flexural Strength	137 MPa	19900 psi	2.8 mm/min; ASTM D790
Samsung Cheil Industries InfinoÂ® LS-1150G PC/ABS, 15% Glass Filled FR 15% GF reinforcement; can be used in mold frames for LCD BLU.Information provided by Samsung Cheil Industries.
Flexural Strength	137 MPa	19900 psi	2.8 mm/min; ASTM D790
Samsung Cheil Industries StarexÂ® GR-5030FX SAN, Glass Filled Information provided by Samsung Cheil Industries.
Flexural Strength	137 MPa	19900 psi	ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP MF008S PP LNP THERMOCOMP* MF008S is a compound based on Polypropylene resin containing 30% Glass Fiber. Added features of this material include: Chemically Coupled, Heat Stabilized.
Flexural Strength	137 MPa	19900 psi	2.8 mm/min; ASTM D790
Samsung Cheil Industries InfinoÂ® LS-3104G PC, 10% Glass Filled High Impact High-impact resistant PC/GF with 10% GF reinforcement for LCD BLFInformation provided by Samsung Cheil Industries.
Flexural Strength	137 MPa	19900 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP WF0039U PBT LNP* THERMOCOMP* WF0039U is a compound based on PBT resin containing 15% Glass Fiber. Added features of this grade include: Flame Retardant and UV Stabilized.
Flexural Strength	137 MPa	19900 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ValoxÂ® 815 PBT (Asia Pacific) 15% GR PBTP, excellent surface finish. Typical applications are hot air gun housing assemblies, industrial glue guns, appliance housings and handles.
Flexural Strength	137 MPa	19900 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP 2C003 ETFE LNP* THERMOCOMP* 2C003 is a compound based on ETFE resin containing 15% Carbon Fiber. Added features of this material include: Electrically Conductive.
Flexural Strength	137 MPa	19900 psi	ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP NF004 PC+ABS LNP* THERMOCOMP* NF004 is a compound based on PC+ABS resin containing 20% Glass Fiber.
Flexural Strength	137 MPa	19900 psi	ASTM D790
A. Schulman SCHULAMID® 66 MF40 Mineral Filled Nylon 66 Information provided by A. Schulman.
Flexural Strength	137 MPa	19900 psi	ISO 178
Polyplastics Duranex® CRN7830 Polybutylene Terephthalate (PBT), Lower noise, 30% GF filled DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers ..
Flexural Strength	137 MPa	19900 psi	ASTM D790
A. Schulman SCHULAMID® 66 MF40 Mineral Filled Nylon 66 Information provided by A. Schulman.
Flexural Strength	137 MPa	19900 psi	20 x 40 mm
CeramTec 192/193 Titania 192/193 is an excellent material for textile and other structural applications, where superior surface finishes are required with high chemical resistance. 193 is identical except it is metallic gra..
Flexural Strength	137 MPa @Temperature 23.0 °C	19900 psi @Temperature 73.4 °F	EN ISO 178
Ensinger TECASINT 4041 Polyimide, Glossy Black, Molybdenum Sulfide (PI) TECASINT is a range of non-melting high temperature polyimides characterized by high strength over a wide range of temperatures, good long term thermal stability, minimal thermal expansion and excel..
Flexural Strength	137 MPa	19900 psi	2.8 mm/min; ASTM D790
Samsung Cheil Industries Infino® NH-3208GL PC, Glass Filled FR Information provided by Samsung Cheil Industries.
Flexural Strength	137 MPa	19900 psi	ASTM D790
LG Chemical IH830 PMMA, General Purpose Grade for Injection Molding Highest of all grades in heat resistanceMechanical strength and surface hardnessParticularly recommended for tail lamp, reflectors, and general lighting fixturesFeatures: Excellent transparency and ..