SABIC Innovative Plastics LNP THERMOCOMP 2C003 ETFE

Category Polymer , Thermoplastic , Fluoropolymer , ETFE/ECTFE
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP 2C003 ETFE.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* THERMOCOMP* 2C003 is a compound based on ETFE resin containing 15% Carbon Fiber. Added features of this material include: Electrically Conductive.
Physical Properties Metric English Comments
Density 1.73 g/cc
0.0625 lb/in³
ASTM D792
Mechanical Properties Metric English Comments
Tensile Strength at Break 90.0 MPa
13100 psi
ASTM D638
90.0 MPa
13100 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 4.9 %
4.9 %
ASTM D638
4.9 %
4.9 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 11.71 GPa
1698 ksi
50 mm/min; ASTM D638
Flexural Strength 137 MPa
19900 psi
ASTM D790
137 MPa
19900 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 11.03 GPa
1600 ksi
ASTM D790
11.03 GPa
1600 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 3.52 J/cm
6.59 ft-lb/in
ASTM D256
Izod Impact, Unnotched 12.38 J/cm
23.19 ft-lb/in
ASTM D4812
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 207 °C

@Thickness 3.20 mm
 405 °F

@Thickness 0.126 in
 unannealed; ASTM D648