Mitsui AURUM® 450 Thermoplastic Polyimide Resin, Non-filled (discontinued **)

Category	Polymer , Thermoplastic , Polyimide, Thermoplastic , Thermoplastic Polyimide, Unfilled
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Mitsui AURUM® 450 Thermoplastic Polyimide Resin, Non-filled (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

AURUM® is an easy melt, processable and recyclable thermoplastic polyimide resin that provides continuous service temperatures to 465° F in its amorphous state and up to 550° F when annealed to its semicrystalline state. In addition, it displays low outgassing, superior radiation resistance and excellent chemical resistance properties.Applications: Components for automotive and aircraft enginesTransmissionFarming, off-road and construction equipmentIndustrial machineryElectric motors, pumps and compressorsBusiness machines such as laser pointers and high speed copy machinesElectronic and semiconductor transport mediaAnalytical and medical equipmentConveyors and textile equipmentInformation provided by Mitsui.

Physical Properties	Metric	English	Comments
Density	1.33 g/cc	0.0480 lb/in³	ASTM D792
Water Absorption	0.34 %	0.34 %	24 hours; ASTM D570
Moisture Absorption at Equilibrium	0.24 %	0.24 %	24 hours, 23°C, 60% RH
Linear Mold Shrinkage	0.0083 cm/cm	0.0083 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell M	95	95	ASTM D785
Hardness, Rockwell R	129	129	ASTM D785
Tensile Strength at Break	92.2 MPa	13400 psi	ASTM D638
Tensile Strength, Ultimate	57.9 MPa @Temperature 150 °C	8400 psi @Temperature 302 °F	ASTM D638
Elongation at Break	90 %	90 %	ASTM D638
	90 % @Temperature 150 °C	90 % @Temperature 302 °F	ASTM D638
Flexural Strength	137 MPa	19900 psi	ASTM D790
	88.3 MPa @Temperature 150 °C	12800 psi @Temperature 302 °F	ASTM D790
Flexural Modulus	2.94 GPa	426 ksi	ASTM D790
	2.55 GPa @Temperature 150 °C	370 ksi @Temperature 302 °F	ASTM D790
Compressive Strength	76.5 MPa @Temperature 150 °C	11100 psi @Temperature 302 °F	JIS K7208
	120 MPa @Temperature 23.0 °C	17400 psi @Temperature 73.4 °F	JIS K7208
Compressive Modulus	1.57 GPa	228 ksi	At 150°C; JIS K7208
	2.16 GPa	313 ksi	At 23°C; JIS K7208
Shear Strength	78.5 MPa @Temperature 150 °C	11400 psi @Temperature 302 °F	JIS K7214
	81.4 MPa @Temperature 23.0 °C	11800 psi @Temperature 73.4 °F	JIS K7214
Izod Impact, Notched	0.883 J/cm	1.65 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
CTE, linear	55.0 µm/m-°C @Temperature 23.0 °C	30.6 µin/in-°F @Temperature 73.4 °F	MD; ASTM D696
	55.0 µm/m-°C @Temperature 200 °C	30.6 µin/in-°F @Temperature 392 °F	MD; ASTM D696
CTE, linear, Transverse to Flow	55.0 µm/m-°C @Temperature 23.0 °C	30.6 µin/in-°F @Temperature 73.4 °F	ASTM D696
	55.0 µm/m-°C @Temperature 200 °C	30.6 µin/in-°F @Temperature 392 °F	ASTM D696
Specific Heat Capacity	1.00 J/g-°C @Temperature 23.0 °C	0.239 BTU/lb-°F @Temperature 73.4 °F	By DSC
	1.00 J/g-°C @Temperature 100 °C	0.239 BTU/lb-°F @Temperature 212 °F	By DSC
	1.42 J/g-°C @Temperature 300 °C	0.339 BTU/lb-°F @Temperature 572 °F	By DSC
Thermal Conductivity	0.174 W/m-K	1.21 BTU-in/hr-ft²-°F
Melting Point	388 °C	730 °F
Maximum Service Temperature, Air	238 °C	460 °F	Heat distortion temperature, load unknown; ASTM D648
Glass Transition Temp, Tg	250 °C	482 °F	By DSC
Decomposition Temperature	570 °C	1060 °F	5% weight reduction temperature, by DTG
Flammability, UL94	V-0 @Thickness 0.400 mm	V-0 @Thickness 0.0157 in	all color
	5VA @Thickness 2.00 mm	5VA @Thickness 0.0787 in	all color
Oxygen Index	47 % @Thickness 3.20 mm	47 % @Thickness 0.126 in	ASTM D256

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+17 - 1.00e+18 ohm-cm	1.00e+17 - 1.00e+18 ohm-cm	ASTM D257
Surface Resistance	1.00e+17 - 1.00e+18 ohm	1.00e+17 - 1.00e+18 ohm	ASTM D257
Dielectric Constant	3.1 @Frequency 1e+6 Hz	3.1 @Frequency 1e+6 Hz	ASTM D150
	3.2 @Frequency 1000 Hz	3.2 @Frequency 1000 Hz	ASTM D150
Dissipation Factor	0.00090 @Frequency 1000 Hz	0.00090 @Frequency 1000 Hz	ASTM D150
	0.0034 @Frequency 1e+6 Hz	0.0034 @Frequency 1e+6 Hz	ASTM D150

Processing Properties	Metric	English	Comments
Processing Temperature	390 - 420 °C	734 - 788 °F	Injection molding, extrusion