SABIC Innovative Plastics LNP THERMOCOMP WF0039U PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP WF0039U PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* WF0039U is a compound based on PBT resin containing 15% Glass Fiber. Added features of this grade include: Flame Retardant and UV Stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.57 g/cc | 0.0567 lb/in³ | ISO 1183 |
| 1.58 g/cc | 0.0571 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.0500 % | 0.0500 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0600 % | 0.0600 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Time 86400 sec |
0.0050 - 0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 95.0 MPa | 13800 psi | Type I, 5 mm/min; ASTM D638 |
| 95.0 MPa | 13800 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 2.3 % | 2.3 % | Type I, 5 mm/min; ASTM D638 |
| 2.3 % | 2.3 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 7.08 GPa | 1030 ksi | 1 mm/min; ISO 527 |
| 7.24 GPa | 1050 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 137 MPa | 19900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 145 MPa | 21000 psi | ISO 178 | |
| Flexural Modulus | 6.06 GPa | 879 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 6.36 GPa | 922 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.480 J/cm | 0.899 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.42 J/cm | 6.41 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 19.0 kJ/m² | 9.04 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 4.00 J @Temperature 23.0 °C |
2.95 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 42.3 µm/m-°C @Temperature -30.0 - 30.0 °C |
23.5 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 107 µm/m-°C @Temperature -30.0 - 30.0 °C |
59.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 212 °C | 414 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 215 °C @Thickness 3.20 mm |
419 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 185 °C | 365 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 194 °C @Thickness 3.20 mm |
381 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Parker Chomerics THERM-A-FORM T647 Cure-in-Place Potting and Underfill Material
- NOVA Chemicals Novapol® LE-0520-A LDPE Extrusion Resin (discontinued **)
- Huntsman Araldite GT 7220 Bisphenol A Epoxy Solid Resin
- Lehmann & Voss LUVOCOM® 1105-7023/GY PEEK, with glass fiber
- A. Schulman COMTUF® 506 Polycarbonate
- Polyram PlusTek PB302G50BK39D Nylon 6, 50% Glass Fiber Reinforced, UV and Heat Stabilized
- ATI Allvac® Nickelvac® 625 Nickel Superalloy, Heat Treatment: 927°C (1700°F) Anneal
- Abatron AboCast 8502-7/AboCure 8502-7 Colorless, Low-Exotherm Epoxy Casting Compound
- CeramTec 848 Zirconia, ZrO2•MgO
- Kraton® D1119 B (SIS) Linear Triblock Copolymer
Copyright © lookpolymers.com All Rights Reserved