SABIC Innovative Plastics LNP Stat-kon DEP32XXC PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Stat-kon DEP32XXC PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP STAT-KON* DEP32XXC is a compound based on Polycarbonate resin containing Carbon Fiber, Silicone, PTFE. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.29 g/cc | 0.0466 lb/in³ | ISO 1183 |
| 1.30 g/cc | 0.0470 lb/in³ | ASTM D 792 | |
| Moisture Absorption at Equilibrium | 0.16 % | 0.16 % | 23°C / 50% RH; ISO 62 |
| 0.10 % @Time 86400 sec |
0.10 % @Time 24.0 hour |
50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm @Time 86400 sec |
0.0010 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.0012 cm/cm @Time 86400 sec |
0.0012 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0015 cm/cm @Time 86400 sec |
0.0015 in/in @Time 24.0 hour |
ISO 294 |
| 0.0020 cm/cm @Time 86400 sec |
0.0020 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 43.0 MPa | 6240 psi | ISO 527 |
| 91.0 MPa | 13200 psi | ASTM D 638 | |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D 638 |
| 3.0 % | 3.0 % | ISO 527 | |
| Tensile Modulus | 7.86 GPa | 1140 ksi | 50 mm/min; ASTM D 638 |
| 7.884 GPa | 1143 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 124 MPa | 18000 psi | ASTM D 790 |
| 137 MPa | 19900 psi | ISO 178 | |
| Flexural Modulus | 5.44 GPa | 789 ksi | ASTM D 790 |
| 6.491 GPa | 941.4 ksi | ISO 178 | |
| Izod Impact, Notched | 0.580 J/cm @Temperature 23.0 °C |
1.09 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 1.97 J/cm @Temperature 23.0 °C |
3.69 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² @Temperature 23.0 °C |
4.28 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 24.0 kJ/m² @Temperature 23.0 °C |
11.4 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 6.00 J | 4.43 ft-lb | Multiaxial Impact; ISO 6603 |
| 16.0 J @Temperature 23.0 °C |
11.8 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 143 °C | 289 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 142 °C @Thickness 3.20 mm |
288 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 100 - 1.00e+6 ohm-cm | 100 - 1.00e+6 ohm-cm | ASTM D 257 |
| Surface Resistance | 100 - 1.00e+6 ohm | 100 - 1.00e+6 ohm | ASTM D 257 |
Users viewing this material also viewed the following:
- PolyOne Maxxam™ PPH-20G Black Polypropylene Homopolymer (PP Homopolymer)
- RheTech Products HP514-01 14% Talc Reinforced High Performance Polypropylene Copolymer, UV Stabilized, Black
- 3M Dyneon™ TFM™ 1705 Modified PTFE Powder (discontinued **)
- Solvay IGEPAL® CO 630 Surfactant
- DuPont Performance Polymers Crastin® S600F10 BK851 Polybutylene Terephthalate (PBT) (Unverified Data**)&l
- Hippe PF CC 202 Woven Cotton Cloth Reinforced Phenolic Resin - Sheet
- Fainplast Compounds PM 5580 Flexible PVC, Lead Free
- Arlon Red Silicone Press Pad with sandwiched Fiberglass Substrate (55393R062)
- DuPont Performance Polymers Minlon® 12T BKB100 Nylon 66 (Unverified Data**)
- Chevron Phillips K-Resin® KR03BR SBC (discontinued **)
Copyright © lookpolymers.com All Rights Reserved