- Polymer Property : Flexural Strength = 275 MPa
Polymer Property : Flexural Strength = 275 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Strength | 275 MPa | 39900 psi | |
| Plastcom SLOVAMID 66 GF 35 HTS PA66, 355% glass fibre, combined stability FeaturesPA 66 for injection moulding, chemically reinforced with 35% glass fibre, heat stabilized and stabilized against hydrolysis. Used for cooling water systems in the automotive industry. Delive.. |
|||
| Flexural Strength | 275 MPa | 39900 psi | |
| Lehmann & Voss LUVOCOM® 19-7416 Polyamide 46, with carbon fiber and PTFE Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Reduced moment of inertia compared with metal parts.Electrically conductive.. |
|||
| Flexural Strength | >= 275 MPa | >= 39900 psi | |
| MarkeTech AO 95 Aluminum Oxide Ceramic Substrate, 95% Purity Data provided by the supplier, MarkeTech International.Substrate Specs: Maximum dimensions 4.0 x 6.0 in.. Thickness 0.12-0.60 in. Surface roughness 0.3 µm as fired; 0.075 µm lapped; 0.025 Â.. |
|||
| Flexural Strength | >= 275 MPa | >= 39900 psi | |
| MarkeTech AO 98 Aluminum Oxide Ceramic Substrate, 98% Purity Data provided by the supplier, MarkeTech International.Substrate Specs: Maximum dimensions 4.0 x 6.0 in.. Thickness 0.12-0.60 in. Surface roughness 0.3 µm as fired; 0.075 µm lapped; 0.025 Â.. |
|||
| Flexural Strength | 275 MPa | 39900 psi | ASTM D790 |
| Kolon KOPA® KN333G30BL G/F Reinforced Nylon 66 G/F 30% reinforcedApplications Engine coversInformation provided by API-Kolon. |
|||
| Flexural Strength | 275 MPa | 39900 psi | ASTM D 790 |
| SABIC Innovative Plastics LNP Lubricomp ICP36 PA 6/12 (Asia Pacific) LNP* Lubricomp* ICP36 is a compound based on Nylon 6/12 resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated, , Electrically Conductive.This data was .. |
|||
| Flexural Strength | 275 MPa | 39900 psi | ISO 178 |
| Solvay TECHNYL® A 218W V30 Black FA PA66, 30% glass fiber, DRY Description: Polyamide 66, reinforced with 30% of glass fiber, for injection molding, heat stabilized, with improved hydrolysis resistance.Available in: EuropeProduct Applications: TECHNYL A 218W V3.. |
|||
| Flexural Strength | 275 MPa | 39900 psi | ISO 178 |
| SABIC Innovative Plastics LNP LUBRICOMP LCL33E PEEK LNP LUBRICOMP* LCL33E is a compound based on Polyetheretherketone resin containing 15% Carbon Fiber, 15% PTFE. Added features of this material include: Easy Molding, Wear Resistant. |
|||
| Flexural Strength | 275 MPa | 39900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP LUBRICOMP RFL26S PA 66 LNP* LUBRICOMP* RFL26S is a compound based on Nylon 66 resin containing 30% Glass Fiber, 10% PTFE. Added features of this material include: Wear Resistant, Heat Stabilized. |
|||
| Flexural Strength | 275 MPa | 39900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP LUBRICOMP UFL36SXC PPA LNP* LUBRICOMP* UFL36SXC is a compound based on Polyphthalamide resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant, Heat Stabilized. |
|||
| Flexural Strength | 275 MPa | 39900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP LUBRICOMP UFL36SXC PPA (Asia Pacific) LNP* Lubricomp* UFL36SXC is a compound based on Polyphthalamide resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated, Heat Stabilized. |
|||
| Flexural Strength | 275 MPa | 39900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP LUBRICOMP UFL36SXQ PPA LNP* LUBRICOMP* UFL36SXQ is a compound based on Polyphthalamide resin containing 30% Glass Fiber, 15%PTFE. Added features of this material include: Wear Resistant, Heat Stabilized, Bearing Grade. |
|||
| Flexural Strength | 275 MPa | 39900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP LUBRICOMP UFL36SXQ PPA (Asia Pacific) LNP* Lubricomp* UFL36SXQ is a compound based on Polyphthalamide resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated, Heat Stabilized. |
|||
| Flexural Strength | 275 MPa | 39900 psi | ISO 178 |
| Solvay Specialty Polymers Amodel® A-1625 HS Polyphthalamide (PPA), 25% GlassCarbon Fiber Amodel® A-1625 HS is a 25% carbon and glass-reinforced, heat-stabilized grade of polyphthalamide (PPA). It is formulated for applications requiring the dissipation of static charge. This material.. |
|||
| Flexural Strength | 275 MPa | 39900 psi | ASTM D790 |
| Solvay Specialty Polymers Amodel® AS-1935 HS Polyphthalamide (PPA), 35% Glass Fiber Amodel® AS-1935 HS is a 35% glass reinforced grade of polyphthalamide (PPA) resin developed specifically for improved performance in a 50/50 ethylene glycol and water environment. This material e.. |
|||
| Flexural Strength | 275 MPa | 39900 psi | ISO 178 |
| Solvay Specialty Polymers Ryton® R-4-222NA Polyphenylene Sulfide (PPS), 40% Glass Fiber Ryton® R-4-222NA 40% glass fiber reinforced polyphenylene sulfide compound provides enhanced mechanical strength after constant or repeated exposure to high temperature water and complies with Un.. |
|||
| Flexural Strength | 275 MPa | 39900 psi | ISO 178 |
| Solvay Specialty Polymers Ryton® R-4-240NA Polyphenylene Sulfide (PPS), 40% Glass Fiber Ryton® R-4-240NA and R-4-240BL 40% glass fiber reinforced polyphenylene sulfide compounds provide enhanced mechanical strength and toughness compared to other polyphenylene sulfide compounds.Feat.. |
|||
| Flexural Strength | 275 MPa | 39900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP EC005R PEI LNP* THERMOCOMP* EC005R is a compound based on Polyetherimide resin containing 25% Carbon Fiber. Added features include: Mold Release, Electrically Conductive. |
|||
| Flexural Strength | 275 MPa | 39900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP RF008H PA 66 LNP* THERMOCOMP* RF008H is a compound based on Nylon 66 containing 40% Glass Fiber. Added feature of this grade is: Healthcare. |
|||
| Flexural Strength | 275 MPa | 39900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP RX10405H PA 66 LNP* Thermocomp* RX10405H is a compound based on Nylon 6/6 containing Carbon Fiber. Characteristics of this grade are: Healthcare. |
|||
| Flexural Strength | 275 MPa | 39900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP STAT-KON EEF42 PEI (Asia Pacific) LNP STAT-KON* EEF42 is a compound based on Polyetherimide resin containing Carbon Fiber, Glass Fiber. Added features of this material include: Electrically Conductive. |
|||
| Flexural Strength | 275 MPa | 39900 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP THERMOCOMP PC006 PA 6 (Europe-Africa-Middle East) LNP* Thermocomp* PC006 is a compound based on Nylon 6 resin containing Carbon Fiber. |
|||
| Flexural Strength | 275 MPa | 39900 psi | ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP UF006S PPA (Asia Pacific) LNP THERMOCOMP* UF006S is a compound based on Polyphthalamide resin containing Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
| Flexural Strength | 275 MPa | 39900 psi | ASTM D790 |
| Polyram PlusTek PA341G9 Nylon 6.6, 45% Glass Fiber 45% glass fiber reinforced, high stiffness and extreme cold environment, UV stabilized polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
| Flexural Strength | 275 MPa | 39900 psi | ISO 178-93 |
| Wellman Wellamid® GF43-66 XE-NBK1 43% Glass Fiber Reinforced, Engineering Grade Nylon 66 Description: Glass Fiber Reinforced, Engineering Grade Nylon 66Information provided by Wellman. |
|||
| Flexural Strength | 275 MPa | 39900 psi | dry; ISO 178 |
| DSM Akulon® K224-G8 PA6-GF40 40% Glass Reinforced |
|||
| Flexural Strength | 275 MPa | 39900 psi | ISO 178 |
| Eurostar Star L PA66 30Y D51 PA66, Carbon Fiber Filled, Injection Molded Star L PA66 30Y D51 is a PTFE Lubricated, Carbon Fiber Reinforced, Polyamide 66 Injection Molding ResinInformation provided by Eurostar. |
|||
| Flexural Strength | 275 MPa @Temperature -40.0 °C |
39900 psi @Temperature -40.0 °F |
ASTM Test |
| BASF Petra® 130 30% Glass Filled PET Petra 130 is a 30% glass fiber reinforced polyethylene terephthalate (PET) for injection molding applications. It exhibits a good combination of performance properties including high strength and s.. |
|||
| Flexural Strength | 275 MPa @Temperature -40.0 °C |
39900 psi @Temperature -40.0 °F |
ASTM Test |
| BASF Petra® 130 FR 30% Glass Filled PET Petra 130 FR is a 30% glass fiber reinforced, flame retardant injection molding polyethylene terephthalate feedstocks. It is recognized as UL 94V-0/5VA by Underwriters Laboratories. It is also avail.. |
|||
| Flexural Strength | 275 MPa | 39900 psi | 2.8mm/min; ASTM D790 |
| Asia International Enterprise (Hong Kong) 60G6 Nylon 66, 30% Filled Information provided by Asia International Enterprise (Hong Kong) Ltd. |
|||