- Samsung Cheil Industries Infino® XF-4150 PPA, Glass Filled
Samsung Cheil Industries Infino® XF-4150 PPA, Glass Filled
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 10% Glass Fiber Reinforced |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Infino® XF-4150 PPA, Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.57 g/cc | 1.57 g/cc | ASTM D792 |
| Water Absorption | 0.30 % @Temperature 23.0 °C |
0.30 % @Temperature 73.4 °F |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm |
0.0010 - 0.0030 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 13 g/10 min @Load 2.16 kg, Temperature 315 °C |
13 g/10 min @Load 4.76 lb, Temperature 599 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 216 MPa | 31300 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 2.7 % | 2.7 % | 5 mm/min; ASTM D638 |
| Flexural Strength | 275 MPa | 39900 psi | 2.8 mm/min; ASTM D638 |
| Flexural Modulus | 13.2 GPa | 1920 ksi | 2.8 mm/min; ASTM D638 |
| Izod Impact, Notched | 1.23 J/cm @Thickness 3.17 mm |
2.30 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 280 °C @Thickness 6.40 mm |
536 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 191 °C | 376 °F | B/50; ISO R306 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics ULTEM AR9300 PEI (Asia Pacific)
- SSAB Tunnplat Docol® 1200 DP High-strength Steel
- Styrolution Novodur® BX13036 ABS + PMMA
- Samsung Cheil Industries Infino® EN-1052 PC, FR
- A. Schulman POLYFORT™ FPP 3063UV-3120 Black, UV Stabilized Modified Polypropylene
- Bhansali Engineering Abstron KU670 ABS Heat Resistant
- Huntsman PE6076 Blow Molding Polyethylene (discontinued **)
- Unifrax Fiberfrax® QF-180™ Blue Coating Cement
- Gwent Electronic Materials C2080415D2 Silver Counter Electrode Paste
Copyright © lookpolymers.com All Rights Reserved