- Eurostar Star L PA66 30Y D51 PA66, Carbon Fiber Filled, Injection Molded
Eurostar Star L PA66 30Y D51 PA66, Carbon Fiber Filled, Injection Molded
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Carbon Fiber Filled |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Star L |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Star L PA66 30Y D51 PA66, Carbon Fiber Filled, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Star L PA66 30Y D51 is a PTFE Lubricated, Carbon Fiber Reinforced, Polyamide 66 Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Thickness 4.00 mm |
0.0010 - 0.0030 in/in @Thickness 0.157 in |
E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 208 MPa | 30200 psi | ISO 527 |
| Elongation at Break | 1.8 % | 1.8 % | ISO 527 |
| Flexural Strength | 275 MPa | 39900 psi | ISO 178 |
| Flexural Modulus | 16.0 GPa | 2320 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80x10x4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 52.0 kJ/m² | 24.7 ft-lb/in² | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 265 °C | 509 °F | ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 243 °C | 469 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 265 - 275 °C | 509 - 527 °F | |
| Zone 2 | 270 - 280 °C | 518 - 536 °F | |
| Zone 3 | 270 - 280 °C | 518 - 536 °F | |
| Melt Temperature | 270 - 280 °C | 518 - 536 °F | |
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | |
| Drying Temperature | 80.0 °C @Time 14400 sec |
176 °F @Time 4.00 hour |
|
| Moisture Content | 0.15 - 0.25 % | 0.15 - 0.25 % |
Users viewing this material also viewed the following:
- Nylene® Norpex® AX290 PPE (Polyphenylene Ether); High Performance High Heat
- PSM Industries Ferro-TiC® MS-5A Age Hardenable Martensitic Stainless Steel
- Haynes HR-160® alloy, plate, aged 4000 hours at 871°C (1600°F)
- Shin-Etsu Silicones KE-9710U Silicone Elastomer
- SABIC Innovative Plastics ULTEM 9076 PEI (Europe-Africa-Middle East)
- Lubrizol Estane® S360D Thermoplastic Polyurethane
- E-Polymers TEKAMID® HG20L 20% Glass Fiber Reinforced High Impact PA/ABS Alloy
- C.O.I.M. PLAXTER® P 80 Low Viscosity Polymeric Plasticizer
- Arlon 47571R007 0.007" (0.178 mm) Uncured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved