Polymer Property : Flexural Strength = 175 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	175 MPa	25400 psi
Plastcom SLOVAMID 6 GF 20 FRG 3 PA6, 20% glass fibre, flame retardant FeaturesPA 6 for injection moulding, chemically reinforced with 20 % glass fibre, with halogen free flame retardant. Main features: flammability in accordance with UL 94 V2 at 1.6 mm, glow wire at 9..
Flexural Strength	175 MPa	25400 psi
Plastcom SLOVAMID 6 GF 35 FRC 5 PA6 reinforced with 35% glass fibre, with flame retardant PA 6 for injection moulding, chemically reinforced with 35 % glass fibre, with halogen free flame retardant. Main features: flammability in accordance with UL 94 V2 at 1.6 mm, glow wire at 750°C, C..
Flexural Strength	175 MPa	25400 psi
Plastcom SLOVAMID 66 GF 15 T 6 TS PA66, 15% glass fibre, 6% talc FeaturesChemically reinforced with 15% glass fibre and 6% of talc, suitable for mouldings with high strength and toughness also at low temperatures. Used in the automotive, engineering and electrica..
Flexural Strength	175 MPa	25400 psi	STN EN ISO 178
Plastcom SLOVAMID® 6 GF 25 E LS PA6 reinforced with glass fiber, UV stabilized PA 6 grade for extrusion, reinforced with 25% glass fiber, determined for extrusion of window profile systems. Delivered in natural as well as full RAL scale color.Information Provided by Plastcom s..
Flexural Strength	175 MPa	25400 psi	ASTM D790
PolyOne Stat-Tech™ PC-15CF/000 Black Polycarbonate (PC) Stat-Tech™ Electrically Conductive Compounds are specifically engineered to provide anti-static, ESD and RFI/EMI shielding performance for critical electronic equipment applications. These compound..
Flexural Strength	<= 175 MPa	<= 25400 psi	ISO 178
Polykemi AB POLYshine PBT D223 GF30 FR PBT, Glass-Fiber Reinforced, Flame Retardant Information provided by Polykemi AB
Flexural Strength	175 MPa	25400 psi
Lehmann & Voss LUVOCOMÂ® 1301-8524 PPS, linear, with glass fiber and PTFE Applications: Automotive industry, textile-and office machinery, medical- and precision engineering.High continuous use and heat distortion temperature. Non flammable.High-strength and stiff parts w..
Flexural Strength	175 MPa	25400 psi
Lehmann & Voss LUVOCOMÂ® 80-7489 Polyacetal-copolymer, with carbon fiber Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts; low thermal coefficient of expansion.Electrically conductive, suitable for..
Flexural Strength	175 MPa	25400 psi	2mm/min; ASTM D790
Kingfa PA6-G15 15% Glass Fiber Reinforced PA6 Features:Good size stabilityLow tendency to wrapHigh mechanical propertiesGood low temperature resistanceGood surfaceExcellent balance propertiesApplications:Injection moldingAutomobile partsPower t..
Flexural Strength	175 MPa	25400 psi	2mm/min; ASTM D790
Kingfa PET-RG20 Flame Retardant, 20% Glass Fiber Reinforced PET Features:Flame retardantHigh strengthGood heat resistanceOutstanding electrical propertiesApplications:Injection moldingConnectorsRelayBobbinsSocketsE & E partsInformation Provided by Kingfa Sci. & ..
Flexural Strength	175 MPa	25400 psi
Lehmann & Voss LUVOCOMÂ® 1301-0915 PPS, linear, with carbon fiber, PTFE, lubricant modified Applications: Automotive industry, textile-and office machinery, medical- and precision engineering.High continuous use and heat distortion temperature. Non flammable.High-strength and stiff parts w..
Flexural Strength	175 MPa	25400 psi	2 mm/min; ISO 178
SABIC Innovative Plastics ValoxÂ® ENH4550 PBT (Asia Pacific) 25% GF reinforced, Non-Brominated & Non-Chlorinated Flame Retardant, PBT resin.
Flexural Strength	175 MPa	25400 psi	ISO 178
Sumitomo Bakelite North America RXÂ® 613 Fiberglass Reinforced Phenolic RXÂ 613 is a fiberglass reinforced phenolic molding compound with good dimensional stability and good strength at elevated temperatures.Information provided by Sumitomo Bak North America, Inc.
Flexural Strength	175 MPa	25400 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP STAT-KON DE003M PC LNP* STAT-KON* DE003M is a compound based on Polycarbonate containing 15% Milled Carbon Fiber. Added feature of this grade is: Electrically Conductive.
Flexural Strength	175 MPa	25400 psi	ASTM D 790
SABIC Innovative Plastics LNP Stat-kon DX02731C PC LNP STAT-KON* DX02731C is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for th..
Flexural Strength	175 MPa	25400 psi	ASTM-D790
Polyram Polytron P40N01 Homopolymer Polypropylene, Chemically Coupled 40% Long Glass Fiber A CHEMICALLY COUPLED 40% LONG GLASS FIBER REINFORCED NATURAL POLYPROPYLENE HEAT STABILIZED FOR INJECTION MOLDING APPLICATION.Information provided by Polyram Ram On Ind.
Flexural Strength	175 MPa	25400 psi	cond; ISO 178
DSM Novamid® 1015G33-8 NAT PA6-GF33 33% Glass Reinforced, Injection Molding
Flexural Strength	175 MPa	25400 psi	ISO 178
DuPont Performance Polymers Crastin® LW9030FR NC010 PBT+ASA (Unverified Data**) 30% Glass Reinforced Flame Retardant Polybutylene Terephthalate Blend with Low Warpage Characteristics Crastin LW9030FR NC010 is a 30% glass fiber reinforced flame retardant polybutylene terephthal..
Flexural Strength	175 MPa	25400 psi	ISO 178
DuPont Performance Polymers Crastin® SK603 BK851 Polybutylene Terephthalate (PBT) (Unverified Data**) 20% Glass Reinforced Polybutylene Terephthalate Crastin SK603 BK851 is a 20% glass fiber reinforced lubricated black polybutylene terephthalate resin for injection molding.Information provided by Du..
Flexural Strength	175 MPa	25400 psi	2 mm/min; ISO 178
Eurostar Starflam AFR450B PA66, 25% Glass Fiber Reinforced, Flame Retardant, Injection Molding Starflam AFR450B is a Flame Retardant, 25% Glass Fiber Reinforced Polyamide 66, Injection Molding ResinInformation provided by Eurostar.
Flexural Strength	175 MPa	25400 psi	2 mm/min; ISO 178
Eurostar Staramide RF006K PA66, Glass Fiber Filled, Injection Molded Staramide RF006K is a Radiation Crosslinkable, Glass Fiber Reinforced Polyamide 66 Injection Molding ResinInformation provided by Eurostar.
Flexural Strength	175 MPa	25400 psi	transverse; ISO 178
Bond Laminates TEPEX® dynalite 102-RGUD600(x)/47% Roving Glass – PA 6 Consolidated Composite Laminate Within the TEPEX® composite laminate, Polyamide 6 is a resin known for its toughness, stiffness, abrasion resistance, heat and chemical resistances. Roving E-Glass fibers have an excellent impact ..
Flexural Strength	175 MPa	25400 psi
Ceradyne Ceralloy® BeO Applications:collector rodshelix supportswindowsFeatures: higher thermal conductivity at room temperature.Information provided by Ceradyne Company
Flexural Strength	175 MPa	25400 psi	ASTM D790
Beijing Chemical Industry KAIFA® HN201-G20 PA6 Resin 20% glass fiber reinforced, thermal resistantInformation provided by Beijing Chemical Industry Research Institute (Group)
Flexural Strength	175 MPa	25400 psi
Lehmann & Voss LUVOCOM® 1106-7742 Polyether imide, with glass fiber, demolding aid Applications: High continuous use and heat distortion temperature. Non flammable.Dynamic stressed parts at high movement velocity.High dimensionally stable precision parts.Information provided by Le..
Flexural Strength	175 MPa	25400 psi	ASTM D790
Unitika RUN35-C25 Weather resistant PA6, Conditioned Weather resistant, noncoating, external exposure-compatibleInformation provided by Unitika Ltd.
Flexural Strength	175 MPa	25400 psi	ASTM D790
Gromax CCP PET 9130-200 30% Glass Filled Product Description: PET glass/mineral 30% reinforced injection molding grade. Characteristics:Excellent electrical property Excellent mechanic and chemical property Excellent weatherability Excell..