DuPont Performance Polymers Crastin® LW9030FR NC010 PBT+ASA  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , PBT + ASA Blend, Glass Fiber Reinforced
Manufacturer DuPont Performance Polymers
Trade Name Crastin®
Port Ningbo port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF DuPont Performance Polymers Crastin® LW9030FR NC010 PBT+ASA  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
30% Glass Reinforced Flame Retardant Polybutylene Terephthalate Blend with Low Warpage Characteristics Crastin LW9030FR NC010 is a 30% glass fiber reinforced flame retardant polybutylene terephthalate blend for injection molding. It has improved surfacInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.42 g/cc
0.0513 lb/in³
1.57 g/cc
0.0567 lb/in³
ISO 1183
Water Absorption 0.72 %
<br>@Thickness 2.00 mm
 0.72 %
<br>@Thickness 0.0787 in
 Sim. to ISO 62
Moisture Absorption 0.210 %
<br>@Thickness 2.00 mm
 0.210 %
<br>@Thickness 0.0787 in
 Sim. to ISO 62
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.0080 cm/cm
0.0080 in/in
ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 125 MPa
18100 psi
ISO 527-1/-2
Tensile Stress 4.04 MPa
<br>@Strain 0.200 %,<br> Temperature 150 °C
 586 psi
<br>@Strain 0.200 %,<br> Temperature 302 °F
 ISO 11403-1 -2
5.165 MPa
<br>@Strain 0.310 %,<br> Temperature 160 °C
 749.1 psi
<br>@Strain 0.310 %,<br> Temperature 320 °F
 ISO 11403-1 -2
12.8 MPa
<br>@Strain 0.940 %,<br> Temperature 150 °C
 1860 psi
<br>@Strain 0.940 %,<br> Temperature 302 °F
 ISO 11403-1 -2
15.5 MPa
<br>@Strain 1.48 %,<br> Temperature 150 °C
 2250 psi
<br>@Strain 1.48 %,<br> Temperature 302 °F
 ISO 11403-1 -2
17.14 MPa
<br>@Strain 2.03 %,<br> Temperature 150 °C
 2486 psi
<br>@Strain 2.03 %,<br> Temperature 302 °F
 ISO 11403-1 -2
17.37 MPa
<br>@Strain 2.935 %,<br> Temperature 160 °C
 2519 psi
<br>@Strain 2.935 %,<br> Temperature 320 °F
 ISO 11403-1 -2
34.95 MPa
<br>@Strain 0.400 %,<br> Temperature 40.0 °C
 5069 psi
<br>@Strain 0.400 %,<br> Temperature 104 °F
 ISO 11403-1 -2
36.17 MPa
<br>@Strain 0.340 %,<br> Temperature 23.0 °C
 5246 psi
<br>@Strain 0.340 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
42.12 MPa
<br>@Strain 0.850 %,<br> Temperature 90.0 °C
 6109 psi
<br>@Strain 0.850 %,<br> Temperature 194 °F
 ISO 11403-1 -2
50.29 MPa
<br>@Strain 1.21 %,<br> Temperature 90.0 °C
 7294 psi
<br>@Strain 1.21 %,<br> Temperature 194 °F
 ISO 11403-1 -2
55.1 MPa
<br>@Strain 1.57 %,<br> Temperature 90.0 °C
 7990 psi
<br>@Strain 1.57 %,<br> Temperature 194 °F
 ISO 11403-1 -2
58.12 MPa
<br>@Strain 1.92 %,<br> Temperature 90.0 °C
 8430 psi
<br>@Strain 1.92 %,<br> Temperature 194 °F
 ISO 11403-1 -2
60.34 MPa
<br>@Strain 0.580 %,<br> Temperature 0.000 °C
 8752 psi
<br>@Strain 0.580 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
74.31 MPa
<br>@Strain 0.710 %,<br> Temperature -20.0 °C
 10780 psi
<br>@Strain 0.710 %,<br> Temperature -4.00 °F
 ISO 11403-1 -2
75.6 MPa
<br>@Strain 1.05 %,<br> Temperature 40.0 °C
 11000 psi
<br>@Strain 1.05 %,<br> Temperature 104 °F
 ISO 11403-1 -2
77.91 MPa
<br>@Strain 0.770 %,<br> Temperature 0.000 °C
 11300 psi
<br>@Strain 0.770 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
87.45 MPa
<br>@Strain 0.960 %,<br> Temperature 23.0 °C
 12680 psi
<br>@Strain 0.960 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
87.68 MPa
<br>@Strain 1.37 %,<br> Temperature 40.0 °C
 12720 psi
<br>@Strain 1.37 %,<br> Temperature 104 °F
 ISO 11403-1 -2
96.93 MPa
<br>@Strain 0.960 %,<br> Temperature -20.0 °C
 14060 psi
<br>@Strain 0.960 %,<br> Temperature -4.00 °F
 ISO 11403-1 -2
96.94 MPa
<br>@Strain 1.77 %,<br> Temperature 40.0 °C
 14060 psi
<br>@Strain 1.77 %,<br> Temperature 104 °F
 ISO 11403-1 -2
98.11 MPa
<br>@Strain 1.03 %,<br> Temperature 0.000 °C
 14230 psi
<br>@Strain 1.03 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
105.41 MPa
<br>@Strain 1.30 %,<br> Temperature 23.0 °C
 15288 psi
<br>@Strain 1.30 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
110.94 MPa
<br>@Strain 1.22 %,<br> Temperature 0.000 °C
 16091 psi
<br>@Strain 1.22 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
114.82 MPa
<br>@Strain 1.57 %,<br> Temperature 23.0 °C
 16653 psi
<br>@Strain 1.57 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
120.22 MPa
<br>@Strain 1.28 %,<br> Temperature -20.0 °C
 17436 psi
<br>@Strain 1.28 %,<br> Temperature -4.00 °F
 ISO 11403-1 -2
Elongation at Break 1.8 %
1.8 %
ISO 527-1/-2
Tensile Modulus 10.5 GPa
1520 ksi
ISO 527-1/-2
1.856 GPa
<br>@Temperature 150 °C
 269.2 ksi
<br>@Temperature 302 °F
 ISO 11403-1 -2
7.46 GPa
<br>@Temperature 60.0 °C
 1080 ksi
<br>@Temperature 140 °F
 ISO 11403-1 -2
11.243 GPa
<br>@Temperature -20.0 °C
 1630.7 ksi
<br>@Temperature -4.00 °F
 ISO 11403-1 -2
Flexural Strength 175 MPa
25400 psi
ISO 178
Secant Modulus 2.275 GPa
<br>@Strain 2.00 %,<br> Temperature 100 °C
 330.0 ksi
<br>@Strain 2.00 %,<br> Temperature 212 °F
 ISO 11403-1 -2
2.756 GPa
<br>@Strain 2.50 %,<br> Temperature 80.0 °C
 399.7 ksi
<br>@Strain 2.50 %,<br> Temperature 176 °F
 ISO 11403-1 -2
4.40 GPa
<br>@Strain 0.250 %,<br> Temperature 100 °C
 638 ksi
<br>@Strain 0.250 %,<br> Temperature 212 °F
 ISO 11403-1 -2
4.94 GPa
<br>@Strain 1.00 %,<br> Temperature 80.0 °C
 716 ksi
<br>@Strain 1.00 %,<br> Temperature 176 °F
 ISO 11403-1 -2
5.14 GPa
<br>@Strain 1.93 %,<br> Temperature 40.0 °C
 746 ksi
<br>@Strain 1.93 %,<br> Temperature 104 °F
 ISO 11403-1 -2
6.02 GPa
<br>@Strain 1.53 %,<br> Temperature 40.0 °C
 872 ksi
<br>@Strain 1.53 %,<br> Temperature 104 °F
 ISO 11403-1 -2
6.89 GPa
<br>@Strain 1.71 %,<br> Temperature 23.0 °C
 1000 ksi
<br>@Strain 1.71 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
7.20 GPa
<br>@Strain 1.05 %,<br> Temperature 40.0 °C
 1040 ksi
<br>@Strain 1.05 %,<br> Temperature 104 °F
 ISO 11403-1 -2
7.9073 GPa
<br>@Strain 1.37 %,<br> Temperature 23.0 °C
 1146.9 ksi
<br>@Strain 1.37 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
8.7375 GPa
<br>@Strain 0.400 %,<br> Temperature 40.0 °C
 1267.3 ksi
<br>@Strain 0.400 %,<br> Temperature 104 °F
 ISO 11403-1 -2
8.75 GPa
<br>@Strain 1.60 %,<br> Temperature -20.0 °C
 1270 ksi
<br>@Strain 1.60 %,<br> Temperature -4.00 °F
 ISO 11403-1 -2
8.77 GPa
<br>@Strain 1.35 %,<br> Temperature 0.000 °C
 1270 ksi
<br>@Strain 1.35 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
9.11 GPa
<br>@Strain 0.960 %,<br> Temperature 23.0 °C
 1320 ksi
<br>@Strain 0.960 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
9.37 GPa
<br>@Strain 1.10 %,<br> Temperature 0.000 °C
 1360 ksi
<br>@Strain 1.10 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
10.1 GPa
<br>@Strain 0.960 %,<br> Temperature -20.0 °C
 1460 ksi
<br>@Strain 0.960 %,<br> Temperature -4.00 °F
 ISO 11403-1 -2
10.1 GPa
<br>@Strain 0.770 %,<br> Temperature 0.000 °C
 1470 ksi
<br>@Strain 0.770 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
10.4 GPa
<br>@Strain 0.580 %,<br> Temperature 0.000 °C
 1510 ksi
<br>@Strain 0.580 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
10.5 GPa
<br>@Strain 0.710 %,<br> Temperature -20.0 °C
 1520 ksi
<br>@Strain 0.710 %,<br> Temperature -4.00 °F
 ISO 11403-1 -2
10.6 GPa
<br>@Strain 0.340 %,<br> Temperature 23.0 °C
 1540 ksi
<br>@Strain 0.340 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
Izod Impact, Notched (ISO) 7.00 kJ/m²
3.33 ft-lb/in²
ISO 180/1A
7.00 kJ/m²
<br>@Temperature -30.0 °C
 3.33 ft-lb/in²
<br>@Temperature -22.0 °F
 ISO 180/1A
Izod Impact, Unnotched (ISO) 35.0 kJ/m²
16.7 ft-lb/in²
ISO 180/1U
35.0 kJ/m²
<br>@Temperature -30.0 °C
 16.7 ft-lb/in²
<br>@Temperature -22.0 °F
 ISO 180/1U
Charpy Impact Unnotched 4.00 J/cm²
19.0 ft-lb/in²
ISO 179/1eU
4.00 J/cm²
<br>@Temperature -30.0 °C
 19.0 ft-lb/in²
<br>@Temperature -22.0 °F
 ISO 179/1eU
Charpy Impact, Notched 0.800 J/cm²
3.81 ft-lb/in²
ISO 179/1eA
0.800 J/cm²
<br>@Temperature -30.0 °C
 3.81 ft-lb/in²
<br>@Temperature -22.0 °F
 ISO 179/1eA