Lehmann & Voss LUVOCOM® 1106-7742 Polyether imide, with glass fiber, demolding aid

Category	Polymer , Thermoplastic , Polyetherimide (PEI) , Polyetherimide (PEI), 10% Glass Fiber
Manufacturer	Lehmann & Voss & Co.
Trade Name	LUVOCOM®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Lehmann & Voss LUVOCOM® 1106-7742 Polyether imide, with glass fiber, demolding aid.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Applications: High continuous use and heat distortion temperature. Non flammable.Dynamic stressed parts at high movement velocity.High dimensionally stable precision parts.Information provided by Lehmann & Voss & Co.KG

Physical Properties	Metric	English	Comments
Specific Gravity	1.38 g/cc	1.38 g/cc	ISO 1183
Water Absorption	<= 0.30 %	<= 0.30 %	23°C/24h
Linear Mold Shrinkage	0.0030 - 0.0070 cm/cm	0.0030 - 0.0070 in/in

Mechanical Properties	Metric	English	Comments
Tensile Stress	125 MPa	18100 psi
Elongation at Yield	3.5 %	3.5 %
	4.5 %	4.5 %	flexural
Modulus of Elasticity	6.00 GPa	870 ksi
Flexural Strength	175 MPa	25400 psi
Flexural Modulus	5.00 GPa	725 ksi
Charpy Impact Unnotched	3.80 J/cm²	18.1 ft-lb/in²	edgewise; ISO 179 1eU

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	170 °C	338 °F

Electrical Properties	Metric	English	Comments
Insulation Resistance	>= 1.00e+12 ohm	>= 1.00e+12 ohm

Processing Properties	Metric	English	Comments
Processing Temperature	380 °C	716 °F	mass temp
Nozzle Temperature	350 - 400 °C	662 - 752 °F
Zone 1	330 - 350 °C	626 - 662 °F
Zone 2	340 - 390 °C	644 - 734 °F
Zone 3	350 - 400 °C	662 - 752 °F
Mold Temperature	150 - 180 °C	302 - 356 °F
Drying Temperature	120 °C @Time >=28800 sec	248 °F @Time >=8.00 hour	Dehumidifying dryer
	150 °C @Time >=14400 sec	302 °F @Time >=4.00 hour	or

Descriptive Properties	Value	Comments
Color	beige