- Kingfa PET-RG20 Flame Retardant, 20% Glass Fiber Reinforced PET
Kingfa PET-RG20 Flame Retardant, 20% Glass Fiber Reinforced PET
| Category | Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), Glass Fiber Filled, Flame Retardant |
| Manufacturer | Kingfa Sci. & Tech. Co. |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kingfa PET-RG20 Flame Retardant, 20% Glass Fiber Reinforced PET.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features:Flame retardantHigh strengthGood heat resistanceOutstanding electrical propertiesApplications:Injection moldingConnectorsRelayBobbinsSocketsE & E partsInformation Provided by Kingfa Sci. & Tech. Co., Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.56 g/cc @Temperature 23.0 °C |
1.56 g/cc @Temperature 73.4 °F |
ASTM D792 |
| Water Absorption | 0.070 % @Temperature 23.0 °C, Time 86400 sec |
0.070 % @Temperature 73.4 °F, Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.010 cm/cm @Temperature 23.0 °C |
0.0020 - 0.010 in/in @Temperature 73.4 °F |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength at Break | 123 MPa | 17800 psi | 10mm/min; ASTM D638 |
| Elongation at Break | 2.6 % | 2.6 % | 10mm/min; ASTM D638 |
| Flexural Strength | 175 MPa | 25400 psi | 2mm/min; ASTM D790 |
| Flexural Modulus | 7.50 GPa | 1090 ksi | 2mm/min; ASTM D790 |
| Izod Impact, Notched | 0.750 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
1.41 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 235 °C @Thickness 6.40 mm |
455 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C @Thickness 6.40 mm |
410 °F @Thickness 0.252 in |
ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
|
| V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | <= 270 °C | <= 518 °F | |
| Rear Barrel Temperature | 235 - 255 °C | 455 - 491 °F | Start Point: 245°C |
| Middle Barrel Temperature | 245 - 265 °C | 473 - 509 °F | Start Point: 250°C |
| Front Barrel Temperature | 255 - 275 °C | 491 - 527 °F | Start Point: 260°C |
| Melt Temperature | 255 - 275 °C | 491 - 527 °F | Start Point: 260°C |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | Start Point: 100°C |
| Drying Temperature | 120 - 140 °C @Time 10800 - 18000 sec |
248 - 284 °F @Time 3.00 - 5.00 hour |
Pre-dry |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Glass Fiber Content (%) | 20 | |
| Injection Speed | Moderate to High |
Users viewing this material also viewed the following:
- DSM Arnitel® UM622 General Purpose Grade Copolyester Elastomer (North America) (discontinued **)
- LNP Thermocomp® UC-1006 Polyphthalamide, Carbon Fiber Reinforcement (discontinued **)
- Nilit FRIANYL B63 H-SG40 Nylon 6 for injection molding, 40% mineral filled
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 6.0 PHR MBTS
- A. Schulman PP 3487-01 Polypropylene Homopolymer Polypropylene
- Dow Corning MOLYKOTE® G-2001
- ChevronTexaco ISO 460 AIO
- CMW® ELKONIUM 32 platinum based alloy
- Parker Chomerics CHO-SEAL® S6600 Conductive Elastomer
Copyright © lookpolymers.com All Rights Reserved