Polymer Property : Flexural Strength = 153 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	153 MPa	22200 psi	ISO 178
SABIC Innovative Plastics LNP LUBRICOMP DFL34 PC LNP LUBRICOMP* DFL34 is a compound based on Polycarbonate resin containing 20% Glass Fiber, 15% PTFE. Added features of this material include: Internally Lubricated.
Flexural Strength	153 MPa	22200 psi	ASTM D790
Solvay Specialty Polymers KetaSpire® KT-880 Polyetheretherketone (PEEK) (Unverified Data**) KetaSpire KT-880 is a high flow grade of unreinforced polyetheretherketone (PEEK) supplied in pellet form. KetaSpire PEEK is produced to the highest industry standards and is characterized by a dist..
Flexural Strength	153 MPa	22200 psi	ASTM D790
Solvay Specialty Polymers KetaSpire® KT-880 NL Polyetheretherketone (PEEK) (Unverified Data**) KetaSpire KT-880 NL is a high flow grade of unreinforced polyetheretherketone (PEEK) supplied in non-lubricated, natural-color pellet form. KetaSpire PEEK is produced to the highest industry standar..
Flexural Strength	153 MPa	22200 psi	ISO 178
SABIC Innovative Plastics LNP LUBRICOMP DFL34H PC LNP LUBRICOMP* DFL34H is a compound based on Polycarbonate resin containing 20% Glass Fiber, 15% PTFE. Added features of this material include: Internally Lubricated, Healthcare.
Flexural Strength	153 MPa	22200 psi	ASTM D790
SABIC Innovative Plastics LNP LUBRILOY DF2041 PC (Asia Pacific) LNP LUBRILOY* DF2041 is a compound based on Polycarbonate resin containing Flame Retardant, Proprietary Lubricant, Glass Fiber. Added features of this material include: Flame Retardant.
Flexural Strength	153 MPa	22200 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP STAT-KON DE0026 PC (Europe-Africa-Middle East) LNP* Stat-kon* DC-1002 FR is a compound based on Polycarbonate resin containing Flame Retardant, Carbon Fiber. Added features of this material include: Flame Retardant, Electrically Conductive.
Flexural Strength	153 MPa	22200 psi	ASTM D790
Solvay Specialty Polymers KetaSpireÂ® KT-880 NL Polyetheretherketone (PEEK) KetaSpireÂ® KT-880 NL is a high flow grade of unreinforced polyetheretherketone (PEEK) supplied in non-lubricated, natural-color pellet form. KetaSpireÂ® PEEK is produced to the highest industry..
Flexural Strength	153 MPa	22200 psi	ASTM D790
Solvay Specialty Polymers KetaSpireÂ® KT-880 Polyetheretherketone (PEEK) KetaSpireÂ® KT-880 is a high flow grade of unreinforced polyetheretherketone (PEEK) supplied in pellet form. KetaSpireÂ® PEEK is produced to the highest industry standards and is characterized b..
Flexural Strength	153 MPa	22200 psi	ASTM D790
Techmer ES HiFillÂ® PEEK GF10 10% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 10% Filler by WeightInformation provided by TP Composites, Inc.
Flexural Strength	153 MPa	22200 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP 9X02540 PC+PET LNP* THERMOCOMP* PDX-02540 is a compound based on a PET+PC Blend containing Proprietary Filler. Flame Retardant.
Flexural Strength	153 MPa	22200 psi	ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP AF006XXZ ABS LNP* THERMOCOMP* AF006XXZ is a compound based on ABS resin containing 30% Glass Fiber.
Flexural Strength	153 MPa	22200 psi	ASTM D790
Techmer ES LuriblendÂ® PA6/6 AF Nylon 66 Availability: North AmericaForms: PelletsFiller/Reinforcement: Aramid FiberAdditive: Heat Stabilizer and LubricantFeatures: Lubricated, Good Wear Resistance, Low Friction and Heat StabilizedInformat..
Flexural Strength	153 MPa	22200 psi	ISO 178
SABIC Innovative Plastics LNP THERMOCOMP RF002XXH PA 66 LNP THERMOCOMP* RF002XXH is a compound based on Nylon 66 resin containing 10% Glass Fiber. Added feature of this material includes: Healthcare.
Flexural Strength	153 MPa	22200 psi	ISO 178
SABIC Innovative Plastics LNP VERTON MV006S PP LNP* VERTON* MV006S is a compound based on Polypropylene resin containing 30% Long Glass Fiber. Added features of this material include: Chemically Coupled, Structural.
Flexural Strength	153 MPa	22200 psi	ISO 178
SABIC Innovative Plastics LNP VERTON MV006S PP (Asia Pacific) LNP VERTON* MV006S is a compound based on Polypropylene resin containing Long Glass. Added features of this material include: Chemically Coupled.
Flexural Strength	153 MPa	22200 psi	ISO 178
SABIC Innovative Plastics LNP VERTON MV006S PP (Europe-Africa-Middle East) LNP VERTON* MV006S is a compound based on Polypropylene resin containing Long Glass. Added features of this material include: Chemically Coupled.
Flexural Strength	153 MPa	22200 psi	ISO 178
SABIC Innovative Plastics LNP VERTON MV006SU PP LNP VERTON* MV006SU is a compound based on Polypropylene resin containing 30% Long Glass Fiber. Added features of this material include: Chemically Coupled, Heat Stabilized, UV Stabilized, Structur..
Flexural Strength	153 MPa	22200 psi	ISO 178
SABIC Innovative Plastics LNP VERTON MV006SU PP (Asia Pacific) LNP VERTON* MV006SU is a compound based on Polypropylene resin containing Long Glass. Added features of this material include: Chemically Coupled.
Flexural Strength	153 MPa	22200 psi	ISO 178
SABIC Innovative Plastics LNP VERTON MV006SU PP (Europe-Africa-Middle East) LNP VERTON* MV006SU is a compound based on Polypropylene resin containing Long Glass. Added features of this material include: Chemically Coupled.
Flexural Strength	153 MPa	22200 psi	2 mm/min; ISO 178
Sax Polymers SAXAMID 226K6 Nylon 6.6, 30% Glass Beads SAXAMID 226K6 is a polyamide 6.6 injection-molding-grade filled with 30% glass beads. It is characterized by optimized shrinkage properties.Information provided by SAX Polymers
Flexural Strength	153 MPa	22200 psi	ASTM D790
A. Schulman ComAlloy® E-12421 Reinforced High Flow Polyamide Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line.
Flexural Strength	153 MPa	22200 psi	ASTM D790
A. Schulman ComAlloy® E-12421 Reinforced High Flow Polyamide Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line.
Flexural Strength	153 MPa	22200 psi	ASTM D790
A. Schulman ComAlloy® E-12421 Reinforced High Flow Polyamide Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line.
Flexural Strength	153 MPa	22200 psi	ASTM D790
A. Schulman ComAlloy® E-12421 Reinforced High Flow Polyamide Information provided by A. Schulman.The ComAlloy product line has been integrated into the A Schulman product line.
Flexural Strength	153 MPa	22200 psi	20% Glass RTM Laminate
TSE Industries EcoSPRAY® 350c Flame-Retardant Polyurethane Resin TSE-EcoSPRAY® 350c is an “Environmentally-Preferred Product” or EPP. It is a Thixotropic flame retardant polyurethane resin free of Styrene, and is an “ultra-low” emitting resin during applica..
Flexural Strength	153 MPa	22200 psi	ASTM D790
A. Schulman ComAlloy Hiloy® 616 Nylon 6, Mineral Reinforced Data provided by the manufacturer, ComAlloy International Company.40% Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Flexural Strength	153 MPa	22200 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP GF004 PSU (Europe-Africa-Middle East) LNP* Thermocomp* GF004 is a compound based on Polysulfone resin containing Glass Fiber.