SABIC Innovative Plastics LNP LUBRILOY DF2041 PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Lubriloy |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRILOY DF2041 PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRILOY* DF2041 is a compound based on Polycarbonate resin containing Flame Retardant, Proprietary Lubricant, Glass Fiber. Added features of this material include: Flame Retardant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0600 % | 0.0600 % | 50% RH, 24 hrs; ASTM D570 |
| 0.110 % | 0.110 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0018 cm/cm @Time 86400 sec |
0.0018 in/in @Time 24.0 hour |
ISO 294 |
| 0.0020 cm/cm @Time 86400 sec |
0.0020 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0039 cm/cm @Time 86400 sec |
0.0039 in/in @Time 24.0 hour |
ISO 294 |
| 0.0040 cm/cm @Time 86400 sec |
0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 100 MPa | 14500 psi | ISO 527 |
| 101 MPa | 14600 psi | ASTM D638 | |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527 |
| 2.2 % | 2.2 % | ASTM D638 | |
| Tensile Modulus | 6.68 GPa | 969 ksi | 50 mm/min; ASTM D638 |
| 6.83 GPa | 991 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 149 MPa | 21600 psi | ISO 178 |
| 153 MPa | 22200 psi | ASTM D790 | |
| Flexural Modulus | 6.27 GPa | 909 ksi | ISO 178 |
| 6.37 GPa | 924 ksi | ASTM D790 | |
| Izod Impact, Notched | 1.54 J/cm | 2.89 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.03 J/cm | 11.3 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 36.0 kJ/m² | 17.1 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 11.0 J | 8.11 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.43 | 0.43 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.36 | 0.36 | ASTM D3702 Modified |
| K (wear) Factor | 115 x 10-8 mm³/N-M | 57.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 102 °C | 216 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 92.0 °C @Thickness 3.20 mm |
198 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPE A 8103 EP BLK
- MV Labs IR410 IrCl3 Iridium(III) chloride, anhydrous
- NIZHNEKAMSKNEFTEKHIM PP 1532B (YD50G) Propylene Homopolymer
- Chevron Phillips Marlex® HHM 5502-02 LD High Density Ethylene Hexene Copolymer with Antistat (discontinued **
- Kennametal Stellite Stellite® 12
- SABIC Innovative Plastics NORYL HM4025H PPE+PS (Asia Pacific)
- Solvay SOPROPHOR® TS/29 Surfactant
- Eurostar Starpylen MX06023 PP, 20% Milled Glass Fiber Filled, Injection Molded
- LG Chemical MA201 ABS, Low Gloss
- KKPC KOSYN KSL 5123 Styrene-Butadiene Latex
Copyright © lookpolymers.com All Rights Reserved