SABIC Innovative Plastics LNP THERMOCOMP AF006XXZ ABS

Category Polymer , Thermoplastic , ABS Polymer
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP AF006XXZ ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* THERMOCOMP* AF006XXZ is a compound based on ABS resin containing 30% Glass Fiber.
Physical Properties Metric English Comments
Density 1.28 g/cc
0.0462 lb/in³
ASTM D792
Linear Mold Shrinkage, Flow 0.0020 cm/cm

@Time 86400 sec
 0.0020 in/in

@Time 24.0 hour
 ASTM D955
Linear Mold Shrinkage, Transverse 0.0040 cm/cm

@Time 86400 sec
 0.0040 in/in

@Time 24.0 hour
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 83.0 MPa
12000 psi
ISO 527
96.0 MPa
13900 psi
ASTM D638
Elongation at Break 1.7 %
1.7 %
ISO 527
1.8 %
1.8 %
ASTM D638
Flexural Strength 119 MPa
17300 psi
ISO 178
153 MPa
22200 psi
ASTM D790
Flexural Modulus 8.00 GPa
1160 ksi
ISO 178
9.17 GPa
1330 ksi
ASTM D790
Izod Impact, Notched 0.580 J/cm
1.09 ft-lb/in
ASTM D256
Izod Impact, Unnotched 2.83 J/cm
5.30 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
80*10*4; ISO 180/1A
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 102 °C
216 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
102 °C

@Thickness 3.20 mm
 216 °F

@Thickness 0.126 in
 unannealed; ASTM D648