SABIC Innovative Plastics LNP VERTON MV006S PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP VERTON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP VERTON MV006S PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* VERTON* MV006S is a compound based on Polypropylene resin containing 30% Long Glass Fiber. Added features of this material include: Chemically Coupled, Structural.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | ISO 1183 |
| 1.13 g/cc | 0.0408 lb/in³ | ASTM D792 | |
| Linear Mold Shrinkage, Flow | 0.0026 cm/cm @Time 86400 sec |
0.0026 in/in @Time 24.0 hour |
ISO 294 |
| 0.0030 cm/cm @Time 86400 sec |
0.0030 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0059 cm/cm @Time 86400 sec |
0.0059 in/in @Time 24.0 hour |
ISO 294 |
| 0.0060 cm/cm @Time 86400 sec |
0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 103 MPa | 14900 psi | ASTM D638 |
| 105 MPa | 15200 psi | ISO 527 | |
| Elongation at Break | 2.6 % | 2.6 % | ASTM D638 |
| 2.6 % | 2.6 % | ISO 527 | |
| Tensile Modulus | 7.81 GPa | 1130 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 150 MPa | 21800 psi | ASTM D790 |
| 153 MPa | 22200 psi | ISO 178 | |
| Flexural Modulus | 6.03 GPa | 875 ksi | ASTM D790 |
| 6.45 GPa | 935 ksi | ISO 178 | |
| Izod Impact, Notched | 1.60 J/cm | 3.00 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.68 J/cm | 14.4 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 18.0 kJ/m² | 8.57 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 49.0 kJ/m² | 23.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 10.0 J | 7.38 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 10.0 J | 7.38 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.36 | 0.36 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.39 | 0.39 | ASTM D3702 Modified |
| K (wear) Factor | 88.6 x 10-8 mm³/N-M | 44.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 18.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
10.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 45.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
25.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 158 °C | 316 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- Nitriflex N-615B NBR - Nitrile Rubber
- 3M Dyneon™ TF 5060 PTFE Dispersion (discontinued **)
- Kennametal Stellite Nucalloy® 488 High-Silicon Nickel-Base Hardfacing Alloy
- Silberline Silvet® 430-30-E1
- DuPont Elvax® 150 Ethylene Vinyl Acetate
- Whitecast Polymer Engineering Epoxy Composite Casting
- Tra-Con Tra-Bond 526M04 Color Keyed High Temperature Epoxy Adhesive
- CTC X-PRO TF 1120 HP Polypropylene Homopolymer, 20% Talc Filled
- Abatron AboCoat 8709-8/AboCure 50-12 Nickel-Filled Electrically Conductive Epoxy Compound
- ArcelorMittal Dual Phase 600 Very high strength steel, Hot Rolled Steel
Copyright © lookpolymers.com All Rights Reserved