Solvay Specialty Polymers KetaSpire® KT-880 Polyetheretherketone (PEEK)

Category Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK)
Manufacturer Solvay Specialty Polymers
Trade Name KetaSpire®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers KetaSpire® KT-880 Polyetheretherketone (PEEK).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
KetaSpire® KT-880 is a high flow grade of unreinforced polyetheretherketone (PEEK) supplied in pellet form. KetaSpire® PEEK is produced to the highest industry standards and is characterized by a distinct combination of properties, which include excellent wear resistance, best-in-class fatigue resistance, ease of melt processing, high purity and excellent chemical resistance to organics, acids and bases.Features: Autoclave Sterilizable; Biocompatible; Ductile; E-beam Sterilizable; Ethylene Oxide Sterilizable; Fatigue Resistant; Flame Retardant; Good Chemical Resistance; Good Dimensional Stability; Good Impact Resistance; Good Sterilizability; Heat Sterilizable; High Flow; High Heat Resistance; Radiation (Gamma) Resistant; Radiation Sterilizable; Radiotranslucent; Steam Resistant; Steam SterilizableUses: Aircraft Applications; Connectors; Dental Applications; Electrical/Electronic Applications; Film; Hospital Goods; Industrial Applications; Medical Devices; Medical/Healthcare Applications; Oil/Gas Applications; Pump Parts; Seals; Surgical InstrumentsInformation provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.30 g/cc
0.0470 lb/in³
ASTM D792
Water Absorption 0.10 %

@Time 86400 sec
 0.10 %

@Time 24.0 hour
 ISO 62
Viscosity 150000 cP

@Shear Rate 1000 1/s,
Temperature 400 °C
 150000 cP

@Shear Rate 1000 1/s,
Temperature 752 °F
 Melt Viscosity; ASTM D3835
Linear Mold Shrinkage, Flow 0.014 - 0.016 cm/cm

@Thickness 3.18 mm
 0.014 - 0.016 in/in

@Thickness 0.125 in
Linear Mold Shrinkage, Transverse 0.015 - 0.017 cm/cm

@Thickness 3.18 mm
 0.015 - 0.017 in/in

@Thickness 0.125 in
 ASTM D955
Melt Flow 36 g/10 min

@Load 2.16 kg,
Temperature 400 °C
 36 g/10 min

@Load 4.76 lb,
Temperature 752 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell M 102
102
ASTM D785
Tensile Strength 100 MPa
14500 psi
50 mm/min; ASTM D638
Tensile Strength, Yield 102 MPa
14800 psi
50 mm/min; ISO 527-2
Elongation at Break 10 - 20 %
10 - 20 %
Type 1A, 50 mm/min; ISO 527-2
10 - 20 %
10 - 20 %
50 mm/min; ASTM D638
Elongation at Yield 5.0 %
5.0 %
Type 1A, 50 mm/min; ISO 527-2
5.2 %
5.2 %
50 mm/min; ASTM D638
Tensile Modulus 3.70 GPa
537 ksi
1.0 mm/min; ASTM D638
4.00 GPa
580 ksi
1 mm/min, Type 1A; ISO 527-2
Flexural Strength 134 MPa
19400 psi
ISO 178
153 MPa
22200 psi
ASTM D790
Flexural Modulus 3.80 GPa
551 ksi
ASTM D790
3.90 GPa
566 ksi
ISO 178
Compressive Strength 123 MPa
17800 psi
ASTM D695
Poissons Ratio 0.37
0.37
ASTM E132
Shear Strength 95.1 MPa
13800 psi
ASTM D732
Izod Impact, Notched 0.530 J/cm
0.993 ft-lb/in
ASTM D256
Izod Impact, Unnotched NB
NB
ASTM D256
Izod Impact, Notched (ISO) 4.90 kJ/m²
2.33 ft-lb/in²
ISO 180
Izod Impact, Unnotched (ISO) NB
NB
ISO 180
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 50.0 µm/m-°C

@Temperature -50.0 - 50.0 °C
 27.8 µin/in-°F

@Temperature -58.0 - 122 °F
 1
Specific Heat Capacity 1.33 J/g-°C

@Temperature 50.0 °C
 0.318 BTU/lb-°F

@Temperature 122 °F
 ASTM C351
1.93 J/g-°C

@Temperature 200 °C
 0.461 BTU/lb-°F

@Temperature 392 °F
 ASTM C351
Thermal Conductivity 0.250 W/m-K
1.74 BTU-in/hr-ft²-°F
ASTM C177
Melting Point 343 °C
649 °F
ASTM D3418
Deflection Temperature at 1.8 MPa (264 psi) 160 °C
320 °F
Annealed; ASTM D648
Glass Transition Temp, Tg 147 °C
297 °F
DSC
Flammability, UL94 V-0

@Thickness >=3.00 mm
 V-0

@Thickness >=0.118 in
Electrical Properties Metric English Comments
Volume Resistivity 3.80e+17 ohm-cm
3.80e+17 ohm-cm
ASTM D257
Surface Resistance >= 1.90e+17 ohm
>= 1.90e+17 ohm
ASTM D257
Dielectric Constant 3.01

@Frequency 1000 Hz
 3.01

@Frequency 1000 Hz
 ASTM D150
3.07

@Frequency 1.00e+6 Hz
 3.07

@Frequency 1.00e+6 Hz
 ASTM D150
3.1

@Frequency 60.0 Hz
 3.1

@Frequency 60.0 Hz
 ASTM D150
Dielectric Strength 15.0 kV/mm

@Thickness 3.00 mm
 381 kV/in

@Thickness 0.118 in
 ASTM D149
Dissipation Factor 0.0010

@Frequency 60.0 Hz
 0.0010

@Frequency 60.0 Hz
 ASTM D150
0.0010

@Frequency 1000 Hz
 0.0010

@Frequency 1000 Hz
 ASTM D150
0.0030

@Frequency 1.00e+6 Hz
 0.0030

@Frequency 1.00e+6 Hz
 ASTM D150
Processing Properties Metric English Comments
Rear Barrel Temperature 355 °C
671 °F
Middle Barrel Temperature 365 °C
689 °F
Front Barrel Temperature 370 °C
698 °F
Nozzle Temperature 375 °C
707 °F
Mold Temperature 175 - 205 °C
347 - 401 °F
Drying Temperature 150 °C

@Time 14400 sec
 302 °F

@Time 4.00 hour
Descriptive Properties Value Comments
Agency Ratings ISO 10993; ISO 10993-Part 1
Availability Africa & Middle East
Asia Pacific
Europe
Latin America
North America
Color Black; Natural
Form Pellets
Injection Rate Fast
Processing Technique Extrusion Blow Molding; Fiber (Spinning) Extrusion
Film Extrusion; Injection Molding
Machining; Profile Extrusion
Thermoforming; Wire & Cable Extrusion
RoHS Compliance RoHS Compliant
Screw Compression Ratio 2.5:1.0 to 3.5:1.0
Users viewing this material also viewed the following: