Polymer Property : Linear Mold Shrinkage, Flow = 0.0090 cm/cm Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Linear Mold Shrinkage, Flow	0.0090 cm/cm @Time 86400 sec	0.0090 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP KONDUIT ITF2B PA 6/12 (Asia Pacific) LNP* Konduit* ITF2B is a compound based on Nylon 6/12 resin containing Glass Fiber, Proprietary Thermal Filler. Added features of this material include: Thermally Conductive.
Linear Mold Shrinkage, Flow	0.0090 cm/cm @Time 86400 sec	0.0090 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP KONDUIT MT00E PP LNP KONDUIT* MT00E is a compound based on Polypropylene resin containing 70% Proprietary Thermal Filler. Added features of this material include: Thermally Conductive.
Linear Mold Shrinkage, Flow	0.0090 cm/cm @Time 86400 sec	0.0090 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP KONDUIT MT00E PP (Asia Pacific) LNP KONDUIT* MT00E is a compound based on Polypropylene resin containing Proprietary Thermal Filler. Added features of this material include: Thermally Conductive.
Linear Mold Shrinkage, Flow	0.0090 cm/cm @Time 86400 sec	0.0090 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP KONDUIT RTF2B PA 66 (Europe-Africa-Middle East) LNP* Konduit* RTF2B is a compound based on Nylon 66 resin containing Glass Fiber, Proprietary Thermal Filler. Added features of this material include: Thermally Conductive.
Linear Mold Shrinkage, Flow	0.0090 cm/cm @Time 86400 sec	0.0090 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP KONDUIT RTF2B PA 66 LNP* KONDUIT* RTF2B is a compound based on Nylon 66 resin containing 10% Glass Fiber, 55% Thermal Filler. Added features of this material include: Thermally Conductive.
Linear Mold Shrinkage, Flow	0.0090 - 0.010 cm/cm @Time 86400 sec	0.0090 - 0.010 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP DP003 PC LNP LUBRICOMP* DP003 is a compound based on Polycarbonate resin containing 15% PTFE/Silicone. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Flow	0.0090 - 0.010 cm/cm @Time 86400 sec	0.0090 - 0.010 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP DP003 PC (Asia Pacific) LNP LUBRICOMP* DP003 is a compound based on Polycarbonate resin containing Silicone, PTFE. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Flow	0.0090 - 0.011 cm/cm @Time 86400 sec	0.0090 - 0.011 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP DX94375H PC LNP* LUBRICOMP* DX94375H is a compound based on Polycarbonate resin containing Proprietary Fillers. Added features of this material include: Healthcare, Wear Resistant.
Linear Mold Shrinkage, Flow	0.0090 - 0.011 cm/cm @Time 86400 sec	0.0090 - 0.011 in/in @Time 24.0 hour	ASTM D 955
SABIC Innovative Plastics LNP Lubricomp EL004 PEI LNP* Lubricomp* EL004 is a compound based on Polyetherimide resin containing PTFE. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for the Americas..
Linear Mold Shrinkage, Flow	0.0090 - 0.011 cm/cm @Time 86400 sec	0.0090 - 0.011 in/in @Time 24.0 hour	ASTM D 955
SABIC Innovative Plastics LNP Lubricomp EL004 PEI (Asia Pacific) LNP* Lubricomp* EL004 is a compound based on Polyetherimide resin containing PTFE. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for the Asia Pac..
Linear Mold Shrinkage, Flow	0.0090 - 0.011 cm/cm @Time 86400 sec	0.0090 - 0.011 in/in @Time 24.0 hour	ASTM D 955
SABIC Innovative Plastics LNP Lubricomp KCL22 Acetal Copoly (Asia Pacific) LNP* Lubricomp* KCL22 is a compound based on Acetal Copolymer resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated, Electrically Conductive.This data ..
Linear Mold Shrinkage, Flow	0.0090 - 0.011 cm/cm @Time 86400 sec	0.0090 - 0.011 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP LUBRICOMP SP003 PA 12 (Asia Pacific) LNP* Lubricomp* SP003 is a compound based on Nylon 12 resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated.
Linear Mold Shrinkage, Flow	0.0090 - 0.016 cm/cm @Thickness 0.750 - 2.30 mm	0.0090 - 0.016 in/in @Thickness 0.0295 - 0.0906 in	SABIC Method
SABIC Innovative Plastics ValoxÂ® 215HPR PBT Unreinforced PBT with mold release. FDA food contact compliant in limited colors. Effective March 2008 this grade will no longer be supported with biocompatibility data. Alternative grade Valox HX21..
Linear Mold Shrinkage, Flow	0.0090 - 0.016 cm/cm @Thickness 0.750 - 2.30 mm	0.0090 - 0.016 in/in @Thickness 0.0295 - 0.0906 in	SABIC Method
SABIC Innovative Plastics ValoxÂ® 295 PBT Unreinforced PBTThis data was supplied by SABIC-IP for the Americas region.
Linear Mold Shrinkage, Flow	0.0090 - 0.016 cm/cm @Thickness 0.750 - 2.30 mm	0.0090 - 0.016 in/in @Thickness 0.0295 - 0.0906 in	SABIC Method
SABIC Innovative Plastics ValoxÂ® 310 PBT Unreinforced, general purpose. Typical viscosity 5000-7000.
Linear Mold Shrinkage, Flow	0.0090 - 0.016 cm/cm @Thickness 0.750 - 2.30 mm	0.0090 - 0.016 in/in @Thickness 0.0295 - 0.0906 in	SABIC Method
SABIC Innovative Plastics ValoxÂ® 310 PBT (Asia Pacific) Unreinforced, general purpose. Typical viscosity 5000-7000.
Linear Mold Shrinkage, Flow	0.0090 - 0.016 cm/cm @Thickness 0.750 - 2.30 mm	0.0090 - 0.016 in/in @Thickness 0.0295 - 0.0906 in	SABIC Method
SABIC Innovative Plastics ValoxÂ® 310HP PBT PBT for compounding/fibers only. Not intended for injection molding. FDA compliant. Available in Natural color (1001) only.
Linear Mold Shrinkage, Flow	0.0090 - 0.016 cm/cm @Thickness 0.750 - 2.30 mm	0.0090 - 0.016 in/in @Thickness 0.0295 - 0.0906 in	SABIC Method
SABIC Innovative Plastics ValoxÂ® 311 PBT Unreinforced, improved resistance to UV. Medium viscosity.
Linear Mold Shrinkage, Flow	0.0090 - 0.016 cm/cm @Thickness 0.750 - 2.30 mm	0.0090 - 0.016 in/in @Thickness 0.0295 - 0.0906 in	SABIC Method
SABIC Innovative Plastics ValoxÂ® 312 PBT Unreinforced, For compounding only (not for injection molding), FDA (21 CFR 177.1660) compliant. Medium viscosity.This data was supplied by SABIC-IP for the Americas region.
Linear Mold Shrinkage, Flow	0.0090 - 0.016 cm/cm @Thickness 0.750 - 2.30 mm	0.0090 - 0.016 in/in @Thickness 0.0295 - 0.0906 in	SABIC Method
SABIC Innovative Plastics ValoxÂ® 312 PBT (Asia Pacific) Unreinforced, For compounding only (not for injection molding), Medium viscosity.
Linear Mold Shrinkage, Flow	0.0090 - 0.016 cm/cm @Thickness 0.750 - 2.30 mm	0.0090 - 0.016 in/in @Thickness 0.0295 - 0.0906 in	SABIC Method
SABIC Innovative Plastics ValoxÂ® 315 PBT Unreinforced, For extrusion/compounding only (not for injection molding). High viscosity. Melt viscosity between 7500 and 9500 poise.
Linear Mold Shrinkage, Flow	0.0090 - 0.016 cm/cm @Thickness 0.750 - 2.30 mm	0.0090 - 0.016 in/in @Thickness 0.0295 - 0.0906 in	SABIC Method
SABIC Innovative Plastics ValoxÂ® 325M PBT (Asia Pacific) 325M is a high flow VALOX 325 for restrictive gate tooling (key buttons)This data was supplied by SABIC-IP for the Asia Pacific region.
Linear Mold Shrinkage, Flow	0.0090 cm/cm @Time 86400 sec	0.0090 in/in @Time 24.0 hour	ASTM D 955
SABIC Innovative Plastics LNP Stat-kon WX98547 PBT LNP* Stat-kon* WX98547 is a compound based on Polybutylene Terephalate resin containing Carbon Powder. Added features of this material include: Electrically Conductive.This data was supplied by SAB..
Linear Mold Shrinkage, Flow	0.0090 cm/cm @Time 86400 sec	0.0090 in/in @Time 24.0 hour	ASTM D 955
SABIC Innovative Plastics LNP Thermocomp MX88073 PP (Asia Pacific) LNP* Thermocomp* MX88073 is a compound based on Polypropylene resin containing Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region.
Linear Mold Shrinkage, Flow	0.0090 - 0.011 cm/cm @Time 86400 sec	0.0090 - 0.011 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP RF0029S PA 66 (Asia Pacific) LNP* Thermocomp* RF0029S is a compound based on Nylon 66 resin containing Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant, Heat Stabilized.
Linear Mold Shrinkage, Flow	0.0090 - 0.011 cm/cm @Time 86400 sec	0.0090 - 0.011 in/in @Time 24.0 hour	ASTM D 955
SABIC Innovative Plastics LNP Lubricomp KCL22 Acetal Copoly LNP* Lubricomp* KCL22 is a compound based on Acetal Copolymer resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated, Electrically Conductive.This data ..
Linear Mold Shrinkage, Flow	0.0090 - 0.011 cm/cm @Time 86400 sec	0.0090 - 0.011 in/in @Time 24.0 hour	ASTM D 955
SABIC Innovative Plastics LNP Thermocomp 9X04488 POLYPHENYLENESULFONE LNP* Thermocomp* 9X04488 is a compound based on POLYPHENYLENESULFONE resin containing Mineral.This data was supplied by SABIC-IP for the Americas region.
Linear Mold Shrinkage, Flow	0.0090 cm/cm @Time 86400 sec	0.0090 in/in @Time 24.0 hour	ASTM D 955
SABIC Innovative Plastics LNP Thermocomp MX88073 PP LNP* Thermocomp* MX88073 is a compound based on Polypropylene resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region.
Linear Mold Shrinkage, Flow	0.0090 - 0.011 cm/cm @Time 86400 sec	0.0090 - 0.011 in/in @Time 24.0 hour	ASTM D 955
SABIC Innovative Plastics LNP Thermocomp OF002A PPS LNP* Thermocomp* OF002A is a compound based on Polyphenylene Sulfide resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region.
Linear Mold Shrinkage, Flow	0.0090 cm/cm @Time 86400 sec	0.0090 in/in @Time 24.0 hour	ASTM D955
SABIC Innovative Plastics LNP THERMOCOMP RX93402 PA 66 LNP THERMOCOMP* RX93402 is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: Flame Retardant.