SABIC Innovative Plastics LNP Lubricomp KCL22 Acetal Copoly

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Carbon Fiber Filled
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Lubricomp KCL22 Acetal Copoly.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Lubricomp* KCL22 is a compound based on Acetal Copolymer resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated, Electrically Conductive.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Density 1.49 g/cc
0.0538 lb/in³
ASTM D 792
1.49 g/cc
0.0538 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.20 %

@Time 86400 sec
 0.20 %

@Time 24.0 hour
 50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.0099 cm/cm

@Time 86400 sec
 0.0099 in/in

@Time 24.0 hour
 ISO 294
0.0090 - 0.011 cm/cm

@Time 86400 sec
 0.0090 - 0.011 in/in

@Time 24.0 hour
 ASTM D 955
Linear Mold Shrinkage, Transverse 0.015 cm/cm

@Time 86400 sec
 0.015 in/in

@Time 24.0 hour
 ISO 294
0.014 - 0.016 cm/cm

@Time 86400 sec
 0.014 - 0.016 in/in

@Time 24.0 hour
 ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 102 MPa
14800 psi
ISO 527
104 MPa
15100 psi
ASTM D 638
Tensile Strength, Yield 103 MPa
14900 psi
ISO 527
104 MPa
15100 psi
ASTM D 638
Elongation at Break 2.0 %
2.0 %
ISO 527
2.1 %
2.1 %
ASTM D 638
Elongation at Yield 2.0 %
2.0 %
ISO 527
2.1 %
2.1 %
ASTM D 638
Tensile Modulus 8.91 GPa
1290 ksi
1 mm/min; ISO 527
8.96 GPa
1300 ksi
50 mm/min; ASTM D 638
Flexural Strength 146 MPa
21200 psi
ISO 178
151 MPa
21900 psi
ASTM D 790
Flexural Modulus 7.58 GPa
1100 ksi
ASTM D 790
7.60 GPa
1100 ksi
ISO 178
Izod Impact, Notched 0.420 J/cm

@Temperature 23.0 °C
 0.787 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Unnotched 4.48 J/cm

@Temperature 23.0 °C
 8.39 ft-lb/in

@Temperature 73.4 °F
 ASTM D 4812
Izod Impact, Notched (ISO) 5.00 kJ/m²

@Temperature 23.0 °C
 2.38 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 25.0 kJ/m²

@Temperature 23.0 °C
 11.9 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1U
Impact Test 2.00 J
1.48 ft-lb
Multiaxial Impact; ISO 6603
9.00 J

@Temperature 23.0 °C
 6.64 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Energy @ peak; ASTM D 3763
Coefficient of Friction, Dynamic 0.36
0.36
ASTM D 3702 Modified
K (wear) Factor 179 x 10-8 mm³/N-M
89.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D 3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 79.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 43.9 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
79.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
 44.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
CTE, linear, Transverse to Flow 66.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
 37.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
67.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 37.2 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 163 °C
325 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
162 °C

@Thickness 3.20 mm
 324 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 158 °C
316 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
161 °C

@Thickness 3.20 mm
 322 °F

@Thickness 0.126 in
 unannealed; ASTM D 648