| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Konduit |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP KONDUIT MT00E PP (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP KONDUIT* MT00E is a compound based on Polypropylene resin containing Proprietary Thermal Filler. Added features of this material include: Thermally Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.94 g/cc | 0.0701 lb/in³ | ISO 1183 |
| 1.952 g/cc | 0.07052 lb/in³ | ASTM D792 | |
| Linear Mold Shrinkage, Flow | 0.0090 cm/cm @Time 86400 sec |
0.0090 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0095 cm/cm @Time 86400 sec |
0.0095 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm @Time 86400 sec |
0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0074 cm/cm @Time 86400 sec |
0.0074 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 22.0 MPa | 3190 psi | ASTM D638 |
| 22.0 MPa | 3190 psi | ISO 527 | |
| Elongation at Break | 0.90 % | 0.90 % | ISO 527 |
| 1.0 % | 1.0 % | ASTM D638 | |
| Tensile Modulus | 8.65 GPa | 1250 ksi | 1 mm/min; ISO 527 |
| 9.073 GPa | 1316 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 44.0 MPa | 6380 psi | ASTM D790 |
| 44.0 MPa | 6380 psi | ISO 178 | |
| Flexural Modulus | 8.16 GPa | 1180 ksi | ISO 178 |
| Izod Impact, Notched | 0.100 J/cm | 0.187 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 0.740 J/cm | 1.39 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1U |
| Coefficient of Friction, Dynamic | 0.43 | 0.43 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.48 | 0.48 | ASTM D3702 Modified |
| K (wear) Factor | 2278 x 10-8 mm³/N-M | 1131 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 1.10 W/m-K | 7.63 BTU-in/hr-ft²-°F | ASTM E 1530 |
| Deflection Temperature at 0.46 MPa (66 psi) | 137 °C | 279 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 103 °C | 217 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- S&E Specialty Polymers G-4285UV PVC
- Fine Organics FINALUX G 200 Lubricant Additive
- Materion BrushCAST® 20CT Fine Grain Casting Alloy (As Cast)
- SABIC Innovative Plastics Ultem SF2250 PEI Blend (Europe-Africa-Middle East)
- BYK Cloisite® 15A Nanoclay
- 3M Scotch-Weld™ HoldFast 70 Cylinder Spray Adhesive
- Industeel VIRGO 17.4PH 17Cr-4Ni-3Cu Precipitation Hardening Martensitic Stainless Steel (480°C (900°F) - 1 hour + air cooled)
Copyright © lookpolymers.com All Rights Reserved