SABIC Innovative Plastics LNP THERMOCOMP RF0029S PA 66 (Asia Pacific)

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP RF0029S PA 66 (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Thermocomp* RF0029S is a compound based on Nylon 66 resin containing Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant, Heat Stabilized.
Physical Properties Metric English Comments
Density 1.48 g/cc
0.0535 lb/in³
ASTM D792
1.48 g/cc
0.0535 lb/in³
ISO 1183
Moisture Absorption 0.500 %
0.500 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.0098 cm/cm

@Time 86400 sec
 0.0098 in/in

@Time 24.0 hour
 ISO 294
0.0090 - 0.011 cm/cm

@Time 86400 sec
 0.0090 - 0.011 in/in

@Time 24.0 hour
 ASTM D955
Linear Mold Shrinkage, Transverse 0.012 - 0.014 cm/cm

@Time 86400 sec
 0.012 - 0.014 in/in

@Time 24.0 hour
 ASTM D955
0.013 cm/cm

@Time 86400 sec
 0.013 in/in

@Time 24.0 hour
 ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 101 MPa
14600 psi
ASTM D638
102 MPa
14800 psi
ISO 527
Tensile Strength, Yield 101 MPa
14600 psi
ASTM D638
102 MPa
14800 psi
ISO 527
Elongation at Break 2.4 %
2.4 %
ISO 527
2.5 %
2.5 %
ASTM D638
Elongation at Yield 2.4 %
2.4 %
ISO 527
2.5 %
2.5 %
ASTM D638
Tensile Modulus 6.37 GPa
924 ksi
1 mm/min; ISO 527
6.89 GPa
999 ksi
50 mm/min; ASTM D638
Flexural Strength 150 MPa
21800 psi
ISO 178
151 MPa
21900 psi
ASTM D790
Flexural Modulus 5.51 GPa
799 ksi
ASTM D790
5.90 GPa
856 ksi
ISO 178
Izod Impact, Notched 0.420 J/cm
0.787 ft-lb/in
ASTM D256
Izod Impact, Unnotched 5.01 J/cm
9.39 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 33.0 kJ/m²
15.7 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 8.00 J
5.90 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 1.00 J
0.738 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 75.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
 42.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
76.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 42.2 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 42.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 23.3 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
43.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
 24.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 249 °C
480 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
252 °C

@Thickness 3.20 mm
 486 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 219 °C
426 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
233 °C

@Thickness 3.20 mm
 451 °F

@Thickness 0.126 in
 unannealed; ASTM D648