SABIC Innovative Plastics Valox® 295 PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® 295 PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Unreinforced PBTThis data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.31 g/cc | 1.31 g/cc | ASTM D 792 |
| Water Absorption | 0.080 % @Time 86400 sec |
0.080 % @Time 24.0 hour |
ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.0090 - 0.016 cm/cm @Thickness 0.750 - 2.30 mm |
0.0090 - 0.016 in/in @Thickness 0.0295 - 0.0906 in |
SABIC Method |
| 0.015 - 0.023 cm/cm @Thickness 2.30 - 4.60 mm |
0.015 - 0.023 in/in @Thickness 0.0906 - 0.181 in |
SABIC Method | |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.017 cm/cm @Thickness 0.750 - 2.30 mm |
0.010 - 0.017 in/in @Thickness 0.0295 - 0.0906 in |
SABIC Method |
| 0.016 - 0.024 cm/cm @Thickness 2.30 - 4.60 mm |
0.016 - 0.024 in/in @Thickness 0.0906 - 0.181 in |
SABIC Method | |
| Melt Flow | 70 g/10 min @Load 2.16 kg, Temperature 250 °C |
70 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 50.0 MPa | 7250 psi | Type I, 50 mm/min; ASTM D 638 |
| Tensile Strength, Yield | 51.0 MPa | 7400 psi | Type I, 50 mm/min; ASTM D 638 |
| Elongation at Break | 14 % | 14 % | Type I, 50 mm/min; ASTM D 638 |
| Elongation at Yield | 3.7 % | 3.7 % | Type I, 50 mm/min; ASTM D 638 |
| Tensile Modulus | 2.67 GPa | 387 ksi | 5 mm/min; ASTM D 638 |
| Flexural Yield Strength | 82.0 MPa | 11900 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 2.34 GPa | 339 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Izod Impact, Notched | 0.530 J/cm @Temperature 23.0 °C |
0.993 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 16.02 J/cm @Temperature 23.0 °C |
30.01 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Gardner Impact | 40.0 J @Temperature 23.0 °C |
29.5 ft-lb @Temperature 73.4 °F |
ASTM D 3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 81.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
45.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 139 µm/m-°C @Temperature 60.0 - 138 °C |
77.2 µin/in-°F @Temperature 140 - 280 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C @Thickness 6.40 mm |
309 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C @Thickness 3.20 mm |
122 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| 54.0 °C @Thickness 6.40 mm |
129 °F @Thickness 0.252 in |
unannealed; ASTM D 648 | |
| Vicat Softening Point | 170 °C | 338 °F | Rate B/50; ASTM D 1525 |
Users viewing this material also viewed the following:
- Plaskolite Optix® CA-81 UVA UV-Absorbing Acrylic Resin
- Carmel Olefins IPETHENE® 214 Low Density Polyethylene (discontinued **)
- Overview of materials for Nylon 11 with 10% Glass Fiber Filler
- Ferro IX 2683 Passivation Glasses - High Voltage (Zn-B-Silicates)
- Shin-Etsu Silicones USPD-2 Fluid
- DuPont Elvax® 3185 Ethylene-Vinyl Acetate Copolymer Resin for Coextrusion
- EMS-Grivory Grivory® TSG-30/4 V0 PA666-GF30 FR
- Fainplast Compounds PHS 60 Flexible PVC, Transparent Extrusion
- Adamas Adalon® 406 PTFE, 15% PEEK
- 3M Scotch® Super 33+™ Vinyl Electrical Tape
Copyright © lookpolymers.com All Rights Reserved