- HOME
- POLYMER SEARCH
- Thermoplastic
- Nylon
- Nylon 612
- SABIC Innovative Plastics LNP KONDUIT ITF2B PA 6/12 (Asia Pacific)
SABIC Innovative Plastics LNP KONDUIT ITF2B PA 6/12 (Asia Pacific)
| Category | Polymer , Thermoplastic , Nylon , Nylon 612 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Konduit |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP KONDUIT ITF2B PA 6/12 (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Konduit* ITF2B is a compound based on Nylon 6/12 resin containing Glass Fiber, Proprietary Thermal Filler. Added features of this material include: Thermally Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Moisture Absorption | 0.120 % | 0.120 % | 23°C / 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0089 cm/cm @Time 86400 sec |
0.0089 in/in @Time 24.0 hour |
ISO 294 |
| 0.0090 cm/cm @Time 86400 sec |
0.0090 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0145 cm/cm @Time 86400 sec |
0.0145 in/in @Time 24.0 hour |
ISO 294 |
| 0.015 cm/cm @Time 86400 sec |
0.015 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 79.0 MPa | 11500 psi | ASTM D638 |
| 80.0 MPa | 11600 psi | ISO 527 | |
| Elongation at Break | 2.1 % | 2.1 % | ASTM D638 |
| 2.2 % | 2.2 % | ISO 527 | |
| Tensile Modulus | 9.98 GPa | 1450 ksi | 50 mm/min; ASTM D638 |
| 10.2 GPa | 1480 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 144 MPa | 20900 psi | ASTM D790 |
| 144 MPa | 20900 psi | ISO 178 | |
| Flexural Modulus | 9.25 GPa | 1340 ksi | ASTM D790 |
| 9.50 GPa | 1380 ksi | ISO 178 | |
| Izod Impact, Notched | 0.320 J/cm | 0.599 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.21 J/cm | 7.89 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 28.0 kJ/m² | 13.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 8.00 J | 5.90 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 1.10 W/m-K | 7.63 BTU-in/hr-ft²-°F | ASTM E 1530 |
| Deflection Temperature at 1.8 MPa (264 psi) | 158 °C | 316 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 167 °C @Thickness 3.20 mm |
333 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- MV Labs PD485 [Pd(NH3)4][PdCl4] Tetraminepalladium(II) tetrachloropalladate(II)
- Resin Technology Group 109-DP Oxy-Bond™ Two-Component Epoxy Adhesive
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 0.0 PHR MBTS
- Kolon KOPEL® KP3855FB Polyester Elastomer Resin (TPE)
- Lubriplate 105 B Tube General Purpose Grease Automotive Lubricant
- Heatbath/Park #3 Granular Charcoal Pack Carburizing Compound
- Diamond Polymers NPP25-0802 GF20 20% Glass Filled Copolymer Polypropylene
- 3M Scotchcal™ 1000-41 Graphic Film
- BASF Ultramid® B3GK24 10/20% Glass Bead/Fiber Filled PA6 (Dry)
- BASF Ultramid® B3UG4 LS Grey 22985 20% Glass Filled PA66 FR (Conditioned)
Copyright © lookpolymers.com All Rights Reserved