Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 0.10 g/10 min @Load 2.16 kg |
0.10 g/10 min @Load 4.76 lb |
ISO 1133 |
Total Lacqtene® 2001 PBK 44 HDPE pipe
(discontinued **) LACQTENE® 2001 PBK 44 is a high density polyethylene produced by the gas phase polymerization process with hexene as comonomer. LACQTENE® 2001 PBK 44 is a black compound especially developed for s.. |
|||
Melt Flow | 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.10 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Iran Petrochemical (PCC) MF3313 High Density Polyethylene MF3313 is a high molecular weight high density polyethylene . Applications: extrusion, film, blown, bags, and density modifies.Information provided by Iran Petrochemical Commercial Co. |
|||
Melt Flow | 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.10 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Iran Petrochemical (PCC) MF3713 High Density Polyethylene MF3713 is a high molecular weight high density polyethylene.Applications: bags, products for use in property modification.Information provided by Iran Petrochemical Commercial Co. |
|||
Melt Flow | 0.10 g/10 min @Load 2.16 kg, Temperature 230 °C |
0.10 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
Kuraray SEPTON® S1001 Thermoplastic Rubber SEPTON® is a series of high performance thermoplastic rubbers developed by Kuraray Co. Ltd. using its isoprene technology. SEPTON® resins are hydrogenated styrenic block copolymers, which exhi.. |
|||
Melt Flow | <= 0.10 g/10 min @Load 2.16 kg, Temperature 230 °C |
<= 0.10 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
Kuraray SEPTON® S4033 Thermoplastic Rubber SEPTON® is a series of high performance thermoplastic rubbers developed by Kuraray Co. Ltd. using its isoprene technology. SEPTON® resins are hydrogenated styrenic block copolymers, which exhi.. |
|||
Melt Flow | <= 0.10 g/10 min @Load 10.0 kg, Temperature 200 °C |
<= 0.10 g/10 min @Load 22.0 lb, Temperature 392 °F |
ISO 1133 |
Kuraray SEPTON® S4033 Thermoplastic Rubber SEPTON® is a series of high performance thermoplastic rubbers developed by Kuraray Co. Ltd. using its isoprene technology. SEPTON® resins are hydrogenated styrenic block copolymers, which exhi.. |
|||
Melt Flow | 0.10 g/10 min @Load 5.00 kg, Temperature 190 °C |
0.10 g/10 min @Load 11.0 lb, Temperature 374 °F |
|
Kazanorgsintez PE2NT 11-9 High Density Polyethylene Composite Production Method: Copolymerization of eythylene at low pressure in presence of complex catalysts using gaseous-phase method. Application: Composition is intended to be processed into pressure p.. |
|||
Melt Flow | 0.10 g/10 min @Load 5.00 kg, Temperature 190 °C |
0.10 g/10 min @Load 11.0 lb, Temperature 374 °F |
ISO 1133 |
Iran Petrochemical (PCC) BL7 HM 6255 High Density Polyethylene BL7 (HM 6255) is a high density polyethylene with Butene-1 as comonomer. It is a special grade for particularly high requirements like low temperature impact strength and stacking, good stress crack.. |
|||
Melt Flow | <= 0.10 g/10 min @Load 2.16 kg, Temperature 230 °C |
<= 0.10 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
Kuraray SEPTON® S8004 Thermoplastic Rubber SEPTON® is a series of high performance thermoplastic rubbers developed by Kuraray Co. Ltd. using its isoprene technology. SEPTON® resins are hydrogenated styrenic block copolymers, which exhi.. |
|||
Melt Flow | <= 0.10 g/10 min @Load 10.0 kg, Temperature 200 °C |
<= 0.10 g/10 min @Load 22.0 lb, Temperature 392 °F |
ISO 1133 |
Kuraray SEPTON® S8004 Thermoplastic Rubber SEPTON® is a series of high performance thermoplastic rubbers developed by Kuraray Co. Ltd. using its isoprene technology. SEPTON® resins are hydrogenated styrenic block copolymers, which exhi.. |
|||
Melt Flow | 0.10 g/10 min @Load 5.00 kg, Temperature 200 °C |
0.10 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
Techmer ES Plastiblend® ABS 8014 Availability: North AmericaForms: PelletsProcessing Method: ExtrusionInformation provided by TP Composites, Inc. |
|||
Melt Flow | 0.10 g/10 min @Load 5.00 kg, Temperature 200 °C |
0.10 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM Test |
Styrolution Terluran® HI-10 ABS Terluran HI-10 is an injection molding and extrusion grade of ABS with very high toughness and medium flow.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS. |
|||
Melt Flow | <= 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C |
<= 0.10 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Topas Advanced Polymers TOPAS® 5013F-04 Cyclic Olefin Copolymer (COC) TOPAS® 5013F-04 is a high temperature film extrusion grade for blends. It is a high clarity amorphous resin with high stiffness, moisture barrier, chemical resistance, thermoformability and purity .. |
|||
Melt Flow | 0.10 g/10 min @Load 2.16 kg |
0.10 g/10 min @Load 4.76 lb |
ISO 1133 |
Total HP 401 MDPE, pipe, cable, sheet FINATHENE® HP 401 is a polyethylene copolymer based on C6 hexene as co-monomer and is produced by a continuous low-pressure slurry polymerization process. FINATHENE® HP 401 is a black high densit.. |
|||
Melt Flow | 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.10 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Chevron Phillips Marlex® HP076 High Density Polyethylene, Pipe Grade This hexene copolymer is tailored for pipe applications that require:Good melt strengthGood pipe stiffnessOutstanding ESCRTypical corrugated pipe applications for HP076 include:Culverts and storm se.. |
|||
Melt Flow | <= 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C |
<= 0.10 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
ExxonMobil HDPE BA53-055 High Density Polyethylene Resin Product Description: BA53-055 is a high molecular weight, high density polyethylene copolymer.Availability: Latin America, North America and South America Additive: Antistatic: NoApplications: Dru.. |
|||
Melt Flow | <= 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C |
<= 0.10 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
ExxonMobil HDPE BU46-055 High Density Polyethylene Resin Product Description: BU46-055 is a high molecular weight, high density polyethylene copolymer which contains a UV inhibitor. It possesses a combination of excellent processability, outstanding melt .. |
|||
Melt Flow | <= 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C |
<= 0.10 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
ExxonMobil HDPE HYA021L High Density Polyethylene Resin Product Description: HYA021L is a molecular weight, high-density polyethylene copolymer. This resin has superior stress crack resistance, high impact strength and good rigidity.Availability: Latin A.. |
|||
Melt Flow | 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.10 g/10 min @Load 4.76 lb, Temperature 374 °F |
ExxonMobil Method |
ExxonMobil Pax-Plus™ 3208 Blown Film Resin Pax-Plus 3208 is a rubber modified high density polyethylene film resin offering good physical properties with ease of processing. It exhibits toughness, stress crack resistance and low WVTR.Inform.. |
|||
Melt Flow | 0.10 g/10 min @Load 5.00 kg, Temperature 200 °C |
0.10 g/10 min @Load 11.0 lb, Temperature 392 °F |
Procedure A Condition G; ASTM D1238 |
Diamond Polymers ABS 3501 GF-30 Description: Reinforced Grade, 30%Glass FilledInformation provided by Diamond Polymers, Inc. |
|||
Melt Flow | 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.10 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Diamond Polymers NPP50-1111 TF20 20% Talc Filled White High Density Polyethylene Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc. |
|||
Melt Flow | 0.10 g/10 min @Load 2.16 kg |
0.10 g/10 min @Load 4.76 lb |
ISO 1133 |
Total Lacqtene® 2001 TBK 46 HDPE pipe
(discontinued **) LACQTENE® 2001 TBK 46 is a high density polyethylene produced by the gas phase polymerization process. LACQTENE® 2001 TBK 46 is a black compound especially developed for pressure pipe for gas and .. |
|||
Melt Flow | 0.10 g/10 min @Load 2.16 kg |
0.10 g/10 min @Load 4.76 lb |
ISO 1133 |
Total Lacqtene® 2001 TN 46 HDPE pipe
(discontinued **) LACQTENE® 2001 TN 46 is a high density polyethylene produced by the gas phase polymerization process with hexene as comonomer. LACQTENE® 2001 TN 46 is used for sewage pipe, smooth protective condu.. |
|||
Melt Flow | 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.10 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Unipetrol PE HD LITEN® VL 29 HDPE Extrusion and pipe applications.Information provided by Unipetrol RPA |
|||
Melt Flow | >= 0.10 g/10 min @Load 2.16 kg, Temperature 190 °C |
>= 0.10 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Borealis Borstar® HE3490-LS Black High Density Polyethylene for Pressure Pipes Borstar HE3490-LS is a black, bimodal, high density polyethylene classified as an MRS 10.0 material (PE100) produced by the advanced Borstar technology. Well dispersed carbon black gives outstanding.. |