- Acrylonitrile Butadiene Styrene (ABS), 30% Glass Fiber Filled
- Diamond Polymers ABS 3501 GF-30
Diamond Polymers ABS 3501 GF-30
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 30% Glass Fiber Filled |
| Manufacturer | Diamond and Network Polymers |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Diamond Polymers ABS 3501 GF-30.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Reinforced Grade, 30%Glass FilledInformation provided by Diamond Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 |
| Melt Flow | 0.10 g/10 min @Load 5.00 kg, Temperature 200 °C |
0.10 g/10 min @Load 11.0 lb, Temperature 392 °F |
Procedure A Condition G; ASTM D1238 |
| 3.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
3.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
Procedure A Condition I; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 78.26 MPa | 11350 psi | chs 2 in/min; ASTM D638 |
| Flexural Modulus | 5.63 GPa | 817 ksi | Procedure B, Test Method I(chs 0.05 in/min); ASTM D790 |
| Izod Impact, Notched | 0.641 J/cm | 1.20 ft-lb/in | Test Method A (0.125 in bar); ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 103 °C | 217 °F | 0.125 in bar Annealed 4 hours at 80°C; ASTM D648 |
| Vicat Softening Point | 115 °C | 239 °F | 0.125 inch, 1 Kg; ASTM D1525 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 190 - 250 °C | 374 - 482 °F | |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | Higher mold temperature provides a product with excellent surface finishing and less residual stress. |
| Drying Temperature | 80.0 - 85.0 °C | 176 - 185 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Injection Pressure | 4.83 - 7.58 MPa | 700 - 1100 psi |
Users viewing this material also viewed the following:
- LG Chemical LUMAX GP5306F PBT+ABS+GF30%, Flame Retardant
- Taiwan PU Corporation PTMG CPU-42L Polyurethane Casting Elastomer
- Silberline Stamford "A1"
- Total PPR 10232 Random Copolymer Polypropylene, Injection Molding
- DSM Novamid® 1013GMF H2 NAT/BK37 PA6-GF30
- Carmel Olefins CAPILENE® SU 75 AV Polypropylene Impact Copolymer
- Tisan TISOPLEN® 25% Glass Fiber Reinforced Flame Retardant (V0). Heat Stabilized Polypropylene
Copyright © lookpolymers.com All Rights Reserved