Chevron Phillips Marlex® HP076 High Density Polyethylene, Pipe Grade

Category	Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Pipe Grade
Manufacturer	Chevron Phillips Chemical Company LP
Trade Name	Marlex®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Chevron Phillips Marlex® HP076 High Density Polyethylene, Pipe Grade.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

This hexene copolymer is tailored for pipe applications that require:Good melt strengthGood pipe stiffnessOutstanding ESCRTypical corrugated pipe applications for HP076 include:Culverts and storm sewersLand drainageConduitThis resin meets or exceeds these specifications:ASTM D4796 - PE 235AASHTO M294ASTM F2160ASTM D3350 class 445540AInformation provided by Chevron Phillips Chemical Company LP.

Physical Properties	Metric	English	Comments
Specific Gravity	0.953 g/cc	0.953 g/cc	ASTM D1505
ESCR 100% Igepal®	>= 600 hour	>= 600 hour	Condition C, f20; ASTM D1693
ESCR 10% Igepal®	>= 1000 hour	>= 1000 hour	Condition B, F50; ASTM D1693
Oxidative Induction Time (OIT)	>= 100 min @Temperature 200 °C	>= 100 min @Temperature 392 °F	ASTM D3895
Melt Flow	0.10 g/10 min @Load 2.16 kg, Temperature 190 °C	0.10 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
	18 g/10 min @Load 21.6 kg, Temperature 190 °C	18 g/10 min @Load 47.6 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	>= 27.0 MPa	>= 3920 psi	2 in/min, Type IV bar; ASTM D638
Elongation at Break	600 %	600 %	2 in/min, Type IV bar; ASTM D638
Flexural Modulus	0.965 GPa	140 ksi	2% Secant; ASTM D790
Tensile Load, Notched Constant	>= 175 hour	>= 175 hour	Ligament Stress, Average of five; ASTM F2136