Total Lacqtene® 2001 TBK 46 HDPE pipe  (discontinued **)

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Pipe Grade
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Total Lacqtene® 2001 TBK 46 HDPE pipe  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LACQTENE® 2001 TBK 46 is a high density polyethylene produced by the gas phase polymerization process. LACQTENE® 2001 TBK 46 is a black compound especially developed for pressure pipe for gas and potable water. LACQTENE® 2001 TBK 46 is best processed between 190 and 230°C.Information provided provided by Total Petrochemicals.Total Petrochemicals includes former Fina and Atofina plastics product lines.
Physical Properties Metric English Comments
Density 0.955 g/cc
0.0345 lb/in³
ISO 1183
Viscosity 1.60e+6 cP

@Shear Rate 100 1/s,
Temperature 190 °C
1.60e+6 cP

@Shear Rate 100 1/s,
Temperature 374 °F
ATOFINA research test
Environmental Stress Crack Resistance >= 700 hour
>= 700 hour
ASTM D1693
Oxidative Induction Time (OIT) >= 20 min
>= 20 min
210°C; EN 728
>= 30 min
>= 30 min
200°C; EN 728
Carbon Black Loading 2.0 - 2.5 %
2.0 - 2.5 %
ISO 6964
Melt Flow 0.10 g/10 min

@Load 2.16 kg
0.10 g/10 min

@Load 4.76 lb
ISO 1133
0.45 g/10 min

@Load 5.00 kg
0.45 g/10 min

@Load 11.0 lb
ISO 1133
High Load Melt Index 12 g/10 min

@Load 21.6 kg
12 g/10 min

@Load 47.6 lb
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 61
61
DIN 53505
Tensile Strength at Break 34.0 MPa
4930 psi
ISO 527
Tensile Strength, Yield 24.0 MPa
3480 psi
ISO 527
Elongation at Break >= 700 %
>= 700 %
ISO 527
Elongation at Yield 9.0 %
9.0 %
ISO 527
Modulus of Elasticity 1.05 GPa
152 ksi
ISO 178
Flexural Modulus 1.00 GPa
145 ksi
ASTM D 790
Thermal Properties Metric English Comments
Heat of Fusion 175 J/g
75.3 BTU/lb
DSC
CTE, linear 160 µm/m-°C

@Temperature 20.0 °C
88.9 µin/in-°F

@Temperature 68.0 °F
Specific Heat Capacity 2.00 J/g-°C
0.478 BTU/lb-°F
DSC
2.60 J/g-°C

@Temperature 150 °C
0.621 BTU/lb-°F

@Temperature 302 °F
DSC
Thermal Conductivity 0.400 W/m-K
2.78 BTU-in/hr-ft²-°F
DIN 52612
0.200 W/m-K

@Temperature 150 °C
1.39 BTU-in/hr-ft²-°F

@Temperature 302 °F
DIN 52612
Melting Point 128 - 131 °C
262 - 268 °F
crystalline; DSC
Vicat Softening Point 127 °C
261 °F
ISO 306
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+16 ohm-cm
>= 1.00e+16 ohm-cm
IEC 93
Dielectric Constant 2.4

@Frequency 1000 Hz
2.4

@Frequency 1000 Hz
IEC 250
Dielectric Strength 18.0 kV/mm
457 kV/in
IEC 243
Descriptive Properties Value Comments
Food Status This material conforms to both European and American Food contact regulations.