Total HP 401 MDPE, pipe, cable, sheet

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Pipe Grade
Manufacturer Total Atofina
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Total HP 401 MDPE, pipe, cable, sheet.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
FINATHENE® HP 401 is a polyethylene copolymer based on C6 hexene as co-monomer and is produced by a continuous low-pressure slurry polymerization process. FINATHENE® HP 401 is a black high density polyethylene specially developed for applications where excellent properties and high stiffness and creep resistance are required (e.g. sewage and drainage pipes, industrial pipes, sheet for chemical storage vessels,.)FINATHENE® HP 401 is a black high density polyethylene developed for cable sheathing applications and is designed to meet the requirements for communication power cables (medium and high voltage cable applications).Information provided provided by Total Petrochemicals.Total Petrochemicals acquired former Fina and Atofina plastics product lines.
Physical Properties Metric English Comments
Density 0.955 g/cc
0.0345 lb/in³
ISO 1183
Environmental Stress Crack Resistance >= 700 hour
>= 700 hour
ASTM D1693
Oxidative Induction Time (OIT) >= 20 min
>= 20 min
210°C; EN 728
>= 30 min
>= 30 min
200°C; EN 728
Carbon Black Loading 2.0 - 2.5 %
2.0 - 2.5 %
ISO 6964
Melt Flow 0.10 g/10 min

@Load 2.16 kg
0.10 g/10 min

@Load 4.76 lb
ISO 1133
0.52 g/10 min

@Load 5.00 kg
0.52 g/10 min

@Load 11.0 lb
ISO 1133
High Load Melt Index 10 g/10 min

@Load 21.6 kg
10 g/10 min

@Load 47.6 lb
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 63
63
DIN 53505
Tensile Strength at Break 34.0 MPa
4930 psi
ISO 527
Tensile Strength, Yield 24.0 MPa
3480 psi
ISO 527
Elongation at Break >= 700 %
>= 700 %
ISO 527
Elongation at Yield 9.0 %
9.0 %
ISO 527
Modulus of Elasticity 1.05 GPa
152 ksi
ISO 178
Flexural Modulus 1.00 GPa
145 ksi
ASTM D 790
Thermal Properties Metric English Comments
Heat of Fusion 175 J/g
75.3 BTU/lb
DSC
CTE, linear 160 µm/m-°C

@Temperature 20.0 °C
88.9 µin/in-°F

@Temperature 68.0 °F
Specific Heat Capacity 2.00 J/g-°C
0.478 BTU/lb-°F
DSC
2.60 J/g-°C

@Temperature 150 °C
0.621 BTU/lb-°F

@Temperature 302 °F
DSC
Thermal Conductivity 0.200 W/m-K

@Temperature 150 °C
1.39 BTU-in/hr-ft²-°F

@Temperature 302 °F
DIN 52612
Vicat Softening Point 127 °C
261 °F
ISO 306
Brittleness Temperature -100 °C
-148 °F
ASTM D 746
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+16 ohm-cm
>= 1.00e+16 ohm-cm
IEC 93
Surface Resistance >= 1.00e+16 ohm
>= 1.00e+16 ohm
IEC 93
Dielectric Constant 2.35

@Frequency 1000 Hz
2.35

@Frequency 1000 Hz
IEC 250
Dielectric Strength 17.0 kV/mm
432 kV/in
IEC 243
Dissipation Factor 0.00020

@Frequency 1000 Hz
0.00020

@Frequency 1000 Hz
IEC 250
0.00030

@Frequency 1e+6 Hz
0.00030

@Frequency 1e+6 Hz
IEC 250