ExxonMobil Pax-Plus™ 3208 Blown Film Resin

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade
Manufacturer	Exxon Chemical
Trade Name	Pax-Plus™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil Pax-Plus™ 3208 Blown Film Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Pax-Plus 3208 is a rubber modified high density polyethylene film resin offering good physical properties with ease of processing. It exhibits toughness, stress crack resistance and low WVTR.Information provided by ExxonMobil Chemical

Physical Properties	Metric	English	Comments
Density	0.936 g/cc	0.0338 lb/in³	ExxonMobil Method
Thickness	50.8 microns	2.00 mil
Melt Flow	0.10 g/10 min @Load 2.16 kg, Temperature 190 °C	0.10 g/10 min @Load 4.76 lb, Temperature 374 °F	ExxonMobil Method
	2.6 g/10 min @Load 10.0 kg, Temperature 190 °C	2.6 g/10 min @Load 22.0 lb, Temperature 374 °F	ExxonMobil Method

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	11.9 MPa	1720 psi	at 2% offset; ASTM D882
Film Tensile Strength at Yield, TD	13.1 MPa	1900 psi	at 2% offset; ASTM D882
Film Elongation at Break, MD	630 %	630 %	ASTM D882
Film Elongation at Break, TD	750 %	750 %	ASTM D882
Puncture Energy	2.135 J	1.575 ft-lb	Exxon Mobil Method
Elmendorf Tear Strength MD	70 g	70 g	ASTM D1922
Elmendorf Tear Strength TD	570 g	570 g	ASTM D1922
Elmendorf Tear Strength, MD	1.38 g/micron	35.0 g/mil	ASTM D1922
Elmendorf Tear Strength, TD	11.2 g/micron	285 g/mil	ASTM D1922
Dart Drop	4.92 g/micron	125 g/mil	ASTM D1709
Dart Drop Test	250 g	0.551 lb	ASTM D1709
Film Tensile Strength at Break, MD	25.7 MPa	3730 psi	ASTM D882
Film Tensile Strength at Break, TD	23.6 MPa	3420 psi	ASTM D882
1% Secant Modulus, MD	325 MPa	47100 psi	ASTM D882
1% Secant Modulus, TD	406 MPa	58900 psi	ASTM D882

Thermal Properties	Metric	English	Comments
Melting Point	128 °C	263 °F	Peak Melting Temperature; ExxonMobil Method
Vicat Softening Point	112 °C	234 °F	ExxonMobil Method

Descriptive Properties	Value	Comments
Features	Thermal Stabilizer