Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 2.0 - 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.0 - 5.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
Procedure A; ASTM D1238 |
PolyOne Maxxam™ FR PE CONC 1 Polyethylene, Low Density (LDPE) Maxxam™ FR flame-retardant polyolefin compounds and masterbatches meet stringent flammability performance requirements defined by industry agencies, including Underwriters Laboratories UL 94 V-2, V.. |
|||
Melt Flow | 3.0 - 5.0 g/10 min @Load 5.00 kg, Temperature 190 °C |
3.0 - 5.0 g/10 min @Load 11.0 lb, Temperature 374 °F |
ISO 1133 |
Polyplastic Armoflen® PO MF 65-1 Linear Low Density Polyethylene, 65% Calcium Carbonate Information provided by PolyPlastic Group. |
|||
Melt Flow | 3.0 - 5.0 g/10 min @Load 5.00 kg, Temperature 190 °C |
3.0 - 5.0 g/10 min @Load 11.0 lb, Temperature 374 °F |
ISO 1133 |
Polyplastic Armoflen® PO MF 65-2 Linear Low Density Polyethylene, 65% Calcium Carbonate Information provided by PolyPlastic Group. |
|||
Melt Flow | 4.0 - 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
4.0 - 5.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Polimeros Mexicanos Rotolene® Black Plus Polyethylene Polyethylene compound specially formulated for rotational molding applications requiring good mechanical properties and good mold release properties. Rotational molded parts have smooth surface and .. |
|||
Melt Flow | 3.0 - 5.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
3.0 - 5.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
NIZHNEKAMSKNEFTEKHIM 825ES High Impact Polystyrene Grade 825ES is a high impact polystyrene designed for extrusion and hot molding application. It is suited for hot molded deep drawn industrial packages and multilayer shaped sheet production via ex.. |
|||
Melt Flow | 0.10 - 5.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
0.10 - 5.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
Polymer Resources ABS-G5 ABS, 5% Glass Reinforced Acrylonitrile Butadiene Styrene, 5% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information .. |
|||
Melt Flow | 1.0 - 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.0 - 5.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
Polymer Resources AC-GP1 Acetal Copolymer, Low Flow, High Melt Strength Process: Molding or ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation. |
|||
Melt Flow | 1.0 - 5.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
1.0 - 5.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
Polymer Resources PC-BR1-UV Polycarbonate, Branched for Extrusion and Blow Molding, UV-stabilized Polycarbonate, Branched for Extrusion and Blow Molding, UV-stabilizedFeatures: • Ultra High Impact Resistance • Ultra High ViscosityProcess: Extrusion/Blow MoldingNotes: All physical, mechanical.. |
|||
Melt Flow | 2.0 - 5.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
2.0 - 5.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
Polymer Resources PC-HH Polycarbonate, High Heat Polycarbonate, High HeatProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resource.. |
|||
Melt Flow | 1.0 - 5.0 g/10 min @Load 2.16 kg, Temperature 250 °C |
1.0 - 5.0 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
Polymer Resources TP-FRHG30 Polybutylene Terephthalate, 30% Glass Reinforced Alloy, Flame Retardant Polybutylene Terephthalate, 30% Glass Reinforced Alloy, Flame RetardantProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test s.. |
|||
Melt Flow | 0.10 - 5.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
0.10 - 5.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
Polymer Resources ABS-G15 ABS, 15% Glass Reinforced Acrylonitrile Butadiene Styrene, 15% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information.. |
|||
Melt Flow | 1.0 - 5.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
1.0 - 5.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
Polymer Resources ABS-GP-HH General Purpose ABS, High Heat General Purpose Acrylonitrile Butadiene Styrene, High HeatProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Inform.. |
|||
Melt Flow | 2.0 - 5.0 g/10 min | 2.0 - 5.0 g/10 min | ASTM D1238-92 |
Iran Petrochemical (PCC) Tabriz 4240/1 High Impact Polystyrene
(discontinued **) Information provided by Iran Petrochemical Commercial Co. |
|||
Melt Flow | 1.0 - 5.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
1.0 - 5.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
Polymer Resources PC-BR1-[color]-5 Polycarbonate, Branched, Food Contact Polycarbonate, Branched for Extrusion and Blow MoldingFeatures: • Ultra High Impact Resistance • Ultra High Viscosity • Food Contact AcceptableProcess: Extrusion/Blow MoldingNotes: All physica.. |
|||
Melt Flow | 3.0 - 5.0 g/10 min @Load 2.16 kg, Temperature 343 °C |
3.0 - 5.0 g/10 min @Load 4.76 lb, Temperature 649 °F |
ASTM D1238 |
Solvay Specialty Polymers Udel® P-3500 LCD Polysulfone (PSU)
(Unverified Data**) Udel P-3500 LCD is a very high molecular weight grade of polysulfone, and therefore offers the greatest toughness and chemical resistance of the available grades. It is well-suited for extrusion. Th.. |
|||
Melt Flow | 1.8 - 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.8 - 5.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Kraton® D1155 B (SBS) Liner Block Copolymer Description: Kraton D1155 B is a clear, linear block copolymer based on styrene and butadiene with bound styrene of 40% mass. It is supplied from South America as indicated in the grade nomenclature.. |
|||
Melt Flow | 2.0 - 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.0 - 5.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
Kraton® G1645 M (SEBS) Linear Triblock Copolymer Description: Kraton G1645 M is a linear triblock copolymer based on styrene and ethylene/butylene. It is supplied from North America in the physical form identified: Kraton G1645 MO - supplied as a .. |
|||
Melt Flow | 2.0 - 5.0 g/10 min | 2.0 - 5.0 g/10 min | (Condition L) ASTM D-1238 |
Multibase Multi-Flex® TPE A 5002 BLK The burn rate is 1 in/min (25 mm/min) based on ASTM FM VSS 302. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
Melt Flow | 2.5 - 5.0 g/10 min | 2.5 - 5.0 g/10 min | (Condition L) ASTM D-1238 |
Multibase Multi-Flex® TPE A 6221 E UV BLK The burn rate is 1 in/min (25 mm/min) based on ASTM FM VSS 302. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
Melt Flow | 2.0 - 5.0 g/10 min @Load 5.00 kg, Temperature 372 °C |
2.0 - 5.0 g/10 min @Load 11.0 lb, Temperature 702 °F |
ASTM D1238 |
Solvay Specialty Polymers Hyflon® PFA M620 Perfluoroalkoxy (PFA) Hyflon® PFA is a unique family of semi-crystalline, melt processable perfluoropolymers which combine excellent mechanical characteristics to unique properties such as chemical inertness, heat res.. |
|||
Melt Flow | 3.0 - 5.0 g/10 min @Load 2.16 kg, Temperature 343 °C |
3.0 - 5.0 g/10 min @Load 4.76 lb, Temperature 649 °F |
ASTM D1238 |
Solvay Specialty Polymers Udel® P-3500 LCD Polysulfone (PSU) Udel® P-3500 LCD is a very high molecular weight grade of polysulfone, and therefore offers the greatest toughness and chemical resistance of the available grades. It is well-suited for extrusion.. |
|||
Melt Flow | 4.0 - 5.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
4.0 - 5.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
Granulate; ISO 1133/H |
SYNTHOS Krasten® FB28 High Impact Polystyrene And Polyethylene Blend Polymer blend HIPS/PE. High toughness, very good tensile properties and environmental stress cracking resistance. Processed mainly by extrusion and thermoforming. Production of sheets and films, tec.. |
|||
Melt Flow | 3.0 - 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
3.0 - 5.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
|
Unitika TERRAMAC TP-4000 Polylactic Acid (PLA) Basic grade, Extrusion, blow, and foam sheet grade. Bio-based materials produced from annually renewable raw materials.Information provided by Unitika Ltd. |
|||
Melt Flow | 3.0 - 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
3.0 - 5.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
|
Unitika TERRAMAC TP-4030 Polylactic Acid (PLA) Soft, Extrusion, blow, and foam sheet grade. Bio-based materials produced from annually renewable raw materials.Information provided by Unitika Ltd. |
|||
Melt Flow | 0.20 - 5.0 g/10 min | 0.20 - 5.0 g/10 min | ASTM D1238 |
Buckeye Polymers BP FLEX 8000 VPL BLK Thermoplastic Elastomer TPV Product Information: BP Flex TPV's are partially vulcanized thermoplastic elastomers designed to meet higher end applications that require the following performance criteria.Product Features:Higher .. |
|||
Melt Flow | 1.0 - 5.0 g/10 min | 1.0 - 5.0 g/10 min | (Condition L) ASTM D-1238 |
Multibase Multi-Flex® TPE A 7606 UV NAT The burn rate is 1 in/min (25 mm/min) based on ASTM FM VSS 302. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
Melt Flow | 2.0 - 5.0 g/10 min @Load 5.00 kg, Temperature 372 °C |
2.0 - 5.0 g/10 min @Load 11.0 lb, Temperature 702 °F |
ASTM D1238 |
Solvay Specialty Polymers Hyflon® PFA M620 Perfluoroalkoxy (PFA)
(Unverified Data**) Hyflon PFA is a unique family of semi-crystalline, melt processable perfluoropolymers which combine excellent mechanical characteristics to unique properties such as chemical inertness, heat resista.. |
|||
Melt Flow | 2.5 - 5.0 g/10 min @Load 5.00 kg, Temperature 372 °C |
2.5 - 5.0 g/10 min @Load 11.0 lb, Temperature 702 °F |
ASTM D1238 |
Solvay Specialty Polymers Hyflon® PFA P220 Perfluoroalkoxy (PFA)
(Unverified Data**) Hyflon® PFA is a unique family of semi-crystalline, melt processable perfluoropolymers which combine excellent mechanical characteristics to unique properties such as chemical inertness, heat resis.. |