SYNTHOS Krasten® FB28 High Impact Polystyrene And Polyethylene Blend
| Category | Polymer , Thermoplastic , Polyethylene (PE) , Polystyrene (PS) |
| Manufacturer | SYNTHOS Kralupy a.s. |
| Trade Name | Krasten® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SYNTHOS Krasten® FB28 High Impact Polystyrene And Polyethylene Blend.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polymer blend HIPS/PE. High toughness, very good tensile properties and environmental stress cracking resistance. Processed mainly by extrusion and thermoforming. Production of sheets and films, technical parts and packaging (e.g. dairy packaging)Synthos was formerly known as Kaucuk. All information provided by Synthos.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.995 g/cc | 0.0359 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in | Internal; 50x50mm |
| Melt Flow | 4.0 - 5.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
4.0 - 5.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
Granulate; ISO 1133/H |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 22.0 MPa @Temperature 23.0 °C |
3190 psi @Temperature 73.4 °F |
50mm/min; ISO 527-2/1A/50 |
| Tensile Strength, Yield | 22.0 MPa @Temperature 23.0 °C |
3190 psi @Temperature 73.4 °F |
50mm/min; ISO 527-2/1A/50 |
| Elongation at Break | 60 % | 60 % | 50mm/min; ISO 527-2/1A/50 |
| Tensile Modulus | 1.20 GPa @Temperature 23.0 °C |
174 ksi @Temperature 73.4 °F |
1mm/min; ISO 527-2/1A/1 |
| Flexural Strength | 30.0 MPa @Temperature 23.0 °C |
4350 psi @Temperature 73.4 °F |
2mm/min; 80x10x4mm; ISO 178 |
| Izod Impact, Notched (ISO) | 24.0 kJ/m² @Temperature 23.0 °C |
11.4 ft-lb/in² @Temperature 73.4 °F |
80x10x4mm, r=0.25; V-notch; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 97.0 kJ/m² @Temperature 23.0 °C |
46.2 ft-lb/in² @Temperature 73.4 °F |
80x10x4mm; ISO 180/1U |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
80x10x4mm; ISO 179/1eU |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
80x10x4mm; ISO 179/1fU | |
| Charpy Impact, Notched | 0.220 J/cm² @Temperature 23.0 °C |
1.05 ft-lb/in² @Temperature 73.4 °F |
80x10x4mm, r=0.25; V-notch; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 68.0 °C | 154 °F | 80x10x4mm; ISO 75-2/Af |
| Vicat Softening Point | 64.0 °C | 147 °F | 50°C/h; 50N; 10x10x4mm; ISO 306/B50 |
| 97.0 °C | 207 °F | 50°C/h; 10N; 10x10x4mm; ISO 306/A50 |
Users viewing this material also viewed the following:
- Multibase Multi-Pro® 2518 CU Polypropylene
- OMG Americas GlidCop® AL-15 Dispersion Strengthened Copper
- Kolon KOPA® KN3311 General Purpose Nylon 66
- Multibase Multi-Flex® TEA 4001-35 Natural TPO Thermoplastic Polyolefin Elastomer
- Sibur Discar-L PC/ABS Compositional Polymer
- Wall Colmonoy COLMONOY® 83 PTA - Nickel-Chromium-Boron Matrix Alloy With Tungsten Carbide
- ExxonMobil LLDPE LL 1002X75 Linear Low Density Polyethylene Resin
- Dow SE SLR-4601 Solution polymerized Styrene Butadiene Rubber (S-SBR)
Copyright © lookpolymers.com All Rights Reserved