- Polymer Resources TP-FRHG30 Polybutylene Terephthalate, 30% Glass Reinforced Alloy, Flame Retardant
Polymer Resources TP-FRHG30 Polybutylene Terephthalate, 30% Glass Reinforced Alloy, Flame Retardant
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled , Polybutylene Terephthalate (PBT), Glass Fiber Filled, Flame Retardant |
| Manufacturer | Polymer Resources, LTD |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polymer Resources TP-FRHG30 Polybutylene Terephthalate, 30% Glass Reinforced Alloy, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polybutylene Terephthalate, 30% Glass Reinforced Alloy, Flame RetardantProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.65 g/cc | 1.65 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 - 0.0090 cm/cm | 0.0030 - 0.0090 in/in | ASTM D955 |
| Melt Flow | 1.0 - 5.0 g/10 min @Load 2.16 kg, Temperature 250 °C |
1.0 - 5.0 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 114 MPa | 16500 psi | ASTM D638 |
| Tensile Strength, Yield | 114 MPa | 16500 psi | ASTM D638 |
| Flexural Strength | 172 MPa | 25000 psi | ASTM D790 |
| Flexural Modulus | 6.89 GPa | 1000 ksi | ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm @Temperature 22.8 °C |
1.00 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 202 °C | 395 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 188 °C | 370 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.59 mm |
V-0 @Thickness 0.0626 in |
|
| V-0 @Thickness 3.17 mm |
V-0 @Thickness 0.125 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 238 - 254 °C | 460 - 490 °F | |
| Middle Barrel Temperature | 243 - 260 °C | 470 - 500 °F | |
| Front Barrel Temperature | 249 - 266 °C | 480 - 510 °F | |
| Melt Temperature | 232 - 260 °C | 450 - 500 °F | |
| Mold Temperature | 71.1 - 87.8 °C | 160 - 190 °F | |
| Drying Temperature | 116 - 121 °C | 240 - 250 °F | |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Vent | 0.0005 |
Users viewing this material also viewed the following:
- Multibase Multi-Pro® 1010 C Natural 10% Filler Content Polypropylene
- Nye Lubricants 362HT (RL) Synthetic Oil
- Ravago Manufacturing Americas Hylon® N1213HL BK Nylon 6/6
- NOVA Chemicals Sclair® 99K Homopolymer HDPE Film Resin
- Borealis Himod™ FT6273 LDPE for Film
- Hexcel® Redux® 340U(SP) (0.01 psf) Modified epoxy film adhesive for bonding metallic and composite components
- CMW® ELKONIUM 301 platinum based alloy
- DuPont Performance Polymers Hytrel® SC988 NC010 TPC-ET (Unverified Data**)
- ChevronTexaco Alcaid® 100
- Lucite International Colacryl ® TS1171 Acrylic Solution Resin
Copyright © lookpolymers.com All Rights Reserved