Unitika TERRAMAC TP-4030 Polylactic Acid (PLA)
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Polylactic Acid (PLA) Biopolymer |
| Manufacturer | Unitika |
| Trade Name | TERRAMAC |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Unitika TERRAMAC TP-4030 Polylactic Acid (PLA).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Soft, Extrusion, blow, and foam sheet grade. Bio-based materials produced from annually renewable raw materials.Information provided by Unitika Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ISO 1183 |
| Melt Flow | 3.0 - 5.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
3.0 - 5.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 50.0 MPa | 7250 psi | ISO 527 |
| Elongation at Break | 44 % | 44 % | ISO 527 |
| Flexural Strength | 71.0 MPa | 10300 psi | ISO 178 |
| Flexural Modulus | 2.40 GPa | 348 ksi | ISO 178 |
| Charpy Impact, Notched | 0.260 J/cm² | 1.24 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 170 °C | 338 °F | |
| Maximum Service Temperature, Air | 240 °C | 464 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 52.0 °C | 126 °F | ISO 75 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 150 - 180 °C | 302 - 356 °F | |
| Middle Barrel Temperature | 160 - 200 °C | 320 - 392 °F | |
| Front Barrel Temperature | 160 - 200 °C | 320 - 392 °F | |
| Nozzle Temperature | 150 - 180 °C | 302 - 356 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Opaque white |
Users viewing this material also viewed the following:
- Polimeri Europa KOBLEND HI 41 PBT+PC, Impact Grade (discontinued **)
- SABIC Innovative Plastics Lexan® 3412 PC (Asia Pacific)
- LG Chemical LI942 Heat Resistant ASA
- LG Chemical LUCON SE-4200H Electrically Conductive Thermoplastic
- GRECO ISOPAK 625 Polycarbonate/ABS Alloy
- Gromax BFG30-FU03B3 Nylon 6 32.9% Glass Filled (Dry)
- Spartech Royalite R60M Hi-Impact ABS/PVC Resin
- Crucible Steel CSM® 6 Tool Steel, AISI A6
- Arlon 51393R031 0.031 (0.635 mm) Cured Silicone Rubber with Fiberglass Substrate
- Asahi Kasei Tenac® 4013A Homopolymer Acetal Resin
Copyright © lookpolymers.com All Rights Reserved