Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 10 - 20 g/10 min | 10 - 20 g/10 min | (Condition L) ASTM D-1238 |
Multibase Multi-Flex® TPE RP 6568 C BLK This product was developed for soft touch airbag covers and contains Kraton G form Shell. The fogging test value is 70% according to ASTM GM 9305P. Multi-Flex TPE contains Kraton™ G.Data provided.. |
|||
Melt Flow | 12 - 20 g/10 min @Load 2.16 kg, Temperature 265 °C |
12 - 20 g/10 min @Load 4.76 lb, Temperature 509 °F |
ASTM D1238 |
Polymer Resources PC/TP-FR3 Flame Retardant PC/Polyester Alloy Flame Retardant, High Impact, Excellent Chemical ResistanceFeatures: • Flame Retardant • Impact Modified • Self Extinguishing • Good Chemical ResistanceProcess: Injection MoldingNotes: All p.. |
|||
Melt Flow | 14 - 20 g/10 min @Load 1.20 kg, Temperature 300 °C |
14 - 20 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
Polymer Resources PC-FD3 Polycarbonate, FDA-compliant Feedstocks, High Flow, Gamma Resistant Polycarbonate, FDA-compliant Feedstocks, High Flow, Gamma ResistantProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test sampl.. |
|||
Melt Flow | 14 - 20 g/10 min @Load 1.20 kg, Temperature 300 °C |
14 - 20 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
Polymer Resources PC-FR3-D-[color]-3 Polycarbonate, Improved Flame Retardant, High Flow, UV-stabilized Polycarbonate, Improved Flame Retardant, High Flow, UV-stabilizedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.. |
|||
Melt Flow | 14 - 20 g/10 min @Load 1.20 kg, Temperature 300 °C |
14 - 20 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
Polymer Resources PC-GP3-D-[color]-6 Polycarbonate, FDA-compliant Feedstocks, High Flow with Mold Release Polycarbonate, FDA-compliant Feedstocks, High Flow with Mold ReleaseProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samp.. |
|||
Melt Flow | 14 - 20 g/10 min @Load 11.6 kg, Temperature 250 °C |
14 - 20 g/10 min @Load 25.6 lb, Temperature 482 °F |
ASTM D1238 |
Polymer Resources PPX-GP8 Modified-PPO, Impact Modified Modified-Polyphenylene Oxide, Impact Modified, 240F HDTProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Informati.. |
|||
Melt Flow | 8.0 - 20 g/10 min @Load 2.16 kg, Temperature 250 °C |
8.0 - 20 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
Polymer Resources TP-G20 Polybutylene Terephthalate, 20% Glass Reinforced Polybutylene Terephthalate, 20% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information prov.. |
|||
Melt Flow | 8.0 - 20 g/10 min @Load 2.16 kg, Temperature 250 °C |
8.0 - 20 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
Polymer Resources TP-G30-TFE15 Polybutylene Terephthalate, 30% Glass Reinforced, 15% PTFE Polybutylene Terephthalate, 30% Glass Reinforced, 15% PTFEProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Inform.. |
|||
Melt Flow | 14 - 20 g/10 min @Load 1.20 kg, Temperature 300 °C |
14 - 20 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
Polymer Resources PC-UV3-D Polycarbonate, UV-stabilized, High Flow Polycarbonate, UV-stabilized, High FlowProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by P.. |
|||
Melt Flow | 15 - 20 g/10 min | 15 - 20 g/10 min | |
Lehmann & Voss LUVOCOM® 50/CF/10/TF/15/BK 100 Polycarbonate, with carbon fiber and PTFE Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.High-strength and high-stiff parts; low coefficient of expansi.. |
|||
Melt Flow | 15 - 20 g/10 min | 15 - 20 g/10 min | 230/2.16 (typical); ASTM D1238 |
Fiberfil® PP-61/TC/20 Polypropylene Copolymer, 20% Talc Information provided by FIBERFIL Engineered Plastics |
|||
Melt Flow | 16 - 20 g/10 min | 16 - 20 g/10 min | 230/2.16; May be specified; ASTM D1238 |
Plastics Group Polifil® RMC-20V 20% Calcium Carbonate-Reinforced Polypropylene, High Impact, UV Stabilized Polifil® RMC-V series compounds are high impact, UV stabilized polypropylenes reinforced with fine particle size calcium carbonate. In addition to the highest impact possible, these compounds retar.. |
|||
Melt Flow | 12 - 20 g/10 min | 12 - 20 g/10 min | ASTM D1238 |
A. Schulman POLYFORT™ FPP 1200H High Flow, Calcium Carbonate Fortified Homopolymer Polypropylene DescriptionPolyfort® FPP 1200H is a high flow 40% calcium carbonate fortified homopolymer polypropylene.Information provided by A. Schulman. |
|||
Melt Flow | 10 - 20 g/10 min | 10 - 20 g/10 min | ASTM D1238 |
A. Schulman POLYFORT™ FPP 1244 Mineral Filled, General Purpose Polypropylene DescriptionPolyfort® FPP 1244 is a 40% mineral filled general purpose polypropylene for parts requiring ultra high stiffness, heat resistance and strength.Information provided by A. Schulman. |
|||
Melt Flow | 15 - 20 g/10 min @Temperature 230 °C |
15 - 20 g/10 min @Temperature 446 °F |
Condition L; ASTM D1238 |
A. Schulman POLYFORT™ FPP 2067HU UV Stabilized, High Heat Resistant Impact Polypropylene DescriptionPolyfort® FPP 2067HU is a unique high flow, UV stabilized high heat resistant impact polypropylene available in matched automotive colors. It molds to a fine appearance with good scrat.. |
|||
Melt Flow | 12 - 20 g/10 min | 12 - 20 g/10 min | ASTM D1238 |
A. Schulman POLYFORT™ FPP 1200H High Flow, Calcium Carbonate Fortified Homopolymer Polypropylene DescriptionPolyfort® FPP 1200H is a high flow 40% calcium carbonate fortified homopolymer polypropylene.Information provided by A. Schulman. |
|||
Melt Flow | 10 - 20 g/10 min | 10 - 20 g/10 min | ASTM D1238 |
A. Schulman POLYFORT™ FPP 1244 Mineral Filled, General Purpose Polypropylene DescriptionPolyfort® FPP 1244 is a 40% mineral filled general purpose polypropylene for parts requiring ultra high stiffness, heat resistance and strength.Information provided by A. Schulman. |
|||
Melt Flow | 12 - 20 g/10 min | 12 - 20 g/10 min | 300/1.2; May be specified; ASTM D1238 |
Plastics Group Polifil® GFPC-30 30% Glass-Reinforced Polycarbonate Polifil® GFPC series compounds offer a combination of improved dimensional stability and decreased flammability. The excellent balance of physical properties make the Polifil® glass-filled polycar.. |
|||
Melt Flow | 12 - 20 g/10 min | 12 - 20 g/10 min | 300/1.2; May be specified; ASTM D1238 |
Plastics Group Polifil® GFPC-40 40% Glass-Reinforced Polycarbonate Polifil® GFPC series compounds offer a combination of improved dimensional stability and decreased flammability. The excellent balance of physical properties make the Polifil® glass-filled polycar.. |
|||
Melt Flow | 14 - 20 g/10 min @Load 2.16 kg, Temperature 230 °C |
14 - 20 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
Cresset Powers Cress-Alon™ A2600 2.6 r.v. Compounding Grade Nylon 6, Dry As Molded Neat resin, for compounding.Information provided by Cresset Powers Ltd. |
|||
Melt Flow | 14 - 20 g/10 min @Load 2.16 kg, Temperature 230 °C |
14 - 20 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
Cresset Powers Cress-Alon™ A2700 2.7 r.v. Compounding Grade Nylon 6, 50% RH Neat resin, for compounding.Information provided by Cresset Powers Ltd. |
|||
Melt Flow | 14 - 20 g/10 min | 14 - 20 g/10 min | ASTM D1238 |
Buckeye Polymers BP FLEX D6020 BLK Thermoplastic Polyolefin Product Information: TPO's are a family of thermoplastic elastomers which exhibit rubber-like properties and are processable on conventional thermoplastic equipment.Product Features:High tear resist.. |
|||
Melt Flow | 14 - 20 g/10 min | 14 - 20 g/10 min | ASTM D1238 |
Buckeye Polymers BP FLEX D6020 U BLK Thermoplastic Polyolefin Product Information: TPO's are a family of thermoplastic elastomers which exhibit rubber-like properties and are processable on conventional thermoplastic equipment.Product Features:High tear resist.. |
|||
Melt Flow | 10 - 20 g/10 min | 10 - 20 g/10 min | ASTM D359 |
Asahi Glass Fluon® LM-720AP LM-ETFE Fluororesin Fluon®LM-ETFE combines the excellent properties in heat resistance and other mechanical properties owned by ETFE resin and the low melting point.Information provided by Asahi Glass Company, Inc. |
|||
Melt Flow | 16 - 20 g/10 min | 16 - 20 g/10 min | 230/2.16; May be specified; ASTM D1238 |
Plastics Group Polifil® RMT-40V 40% Talc-Reinforced Polypropylene, High Impact, UV Stabilized Polifil® RMT-V series compounds are high impact, UV stabilized polypropylenes reinforced with asbestos-free talc. In addition to high impact strength, they possess a high flex modulus and the abili.. |
|||
Melt Flow | 10 - 20 g/10 min | 10 - 20 g/10 min | 230/2.16; May be specified; ASTM D1238 |
Plastics Group Polifil® RP-PP Polypropylene, Molding Grade Polifil® RP-PP reprocessed polypropylene has the highest stiffness of the commodity olefin resins, while retaining sufficient impact properties for many applications. Due to its low cost and low de.. |
|||
Melt Flow | 16.1 - 20 g/10 min | 16.1 - 20 g/10 min | A |
Shandong Dongyue Shenzhou New Material Co DS608 Fluorinated Ethylene-Propylene Copolymer For High-Speed Extrusion Conformable with: Q/DYS 003-2007Fluorinated Ethylene Propylene is the copolymer of TFE and HFP, with good thermal stability, outstanding chemical inertness, good electrical insulation, and low coeff.. |
|||
Melt Flow | 16 - 20 g/10 min | 16 - 20 g/10 min | 230/2.16; May be specified; ASTM D1238 |
Plastics Group Polifil® RMT-20V 20% Talc-Reinforced Polypropylene, High Impact, UV Stabilized Polifil® RMT-V series compounds are high impact, UV stabilized polypropylenes reinforced with asbestos-free talc. In addition to high impact strength, they possess a high flex modulus and the abili.. |
|||
Melt Flow | 10 - 20 g/10 min @Load 12.5 kg, Temperature 232 °C |
10 - 20 g/10 min @Load 27.6 lb, Temperature 450 °F |
ASTM D1238 |
Arkema Group KYNAR FLEX® 2850-07 Polyvinylidene Fluoride Copolymer - Extrusion & Molding Characteristics: Natural resin - translucent, off-white hemispheres. 150°C Temperature rating. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechani.. |