Polymer Resources PPX-GP8 Modified-PPO, Impact Modified
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, Molded |
| Manufacturer | Polymer Resources, LTD |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polymer Resources PPX-GP8 Modified-PPO, Impact Modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Modified-Polyphenylene Oxide, Impact Modified, 240F HDTProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 14 - 20 g/10 min @Load 11.6 kg, Temperature 250 °C |
14 - 20 g/10 min @Load 25.6 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 44.8 MPa | 6500 psi | ASTM D638 |
| Tensile Strength, Yield | 44.8 MPa | 6500 psi | ASTM D638 |
| Elongation at Break | 50 % | 50 % | ASTM D638 |
| Flexural Strength | 68.9 MPa | 10000 psi | ASTM D790 |
| Flexural Modulus | 1.97 GPa | 285 ksi | ASTM D790 |
| Izod Impact, Notched | 1.87 J/cm @Temperature -40.0 °C |
3.50 ft-lb/in @Temperature -40.0 °F |
ASTM D256 |
| 3.74 J/cm @Temperature 22.8 °C |
7.00 ft-lb/in @Temperature 73.0 °F |
ASTM D256 | |
| Gardner Impact | 16.9 J | 12.5 ft-lb | ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 116 °C | 240 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0626 in |
|
| HB @Thickness 3.17 mm |
HB @Thickness 0.125 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 243 - 293 °C | 470 - 560 °F | |
| Middle Barrel Temperature | 254 - 299 °C | 490 - 570 °F | |
| Front Barrel Temperature | 266 - 304 °C | 510 - 580 °F | |
| Melt Temperature | 274 - 302 °C | 525 - 575 °F | |
| Mold Temperature | 65.6 - 98.9 °C | 150 - 210 °F | |
| Drying Temperature | 104 - 110 °C | 220 - 230 °F | |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Vent | 0.0015 |
Users viewing this material also viewed the following:
- RheTech Products HP520-01 12% Talc Reinforced High Performance Polypropylene Copolymer, Non-UV Stabilized, Black
- NOVA Chemicals Gedexcel® 65B Expandable Polystyrene
- Kraton® G1702 + PC blend (5/95)
- Teknor Apex Sarlink® 4475 Thermoplastic Elastomer
- A. Schulman SCHULAMID® 66 GF50 50% Glass Fiber Reinforced 66
- A. Schulman POLYBLAK™ 3209 Superior Black Color Concentrate, 40% Carbon Black Based In Polypropylene
- EMS-Griltech Grilamid® DM 10 Nylon 12 Monofilament
- Arkema Group Rilsan® AECV T8L Nylon 12, Cable Sheathing Grade (Dry)
- Anderman Ceramics EM60 Mullite
- Arkema Group EVATANE® 24-03 Copolymer Ethylene - Vinyl Acetate
Copyright © lookpolymers.com All Rights Reserved