Cresset Powers Cress-Alon™ A2600 2.6 r.v. Compounding Grade Nylon 6, Dry As Molded

Category Polymer , Thermoplastic , Nylon , Nylon 6
Manufacturer Cresset Powers, Ltd
Trade Name Cress-Alon™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Cresset Powers Cress-Alon™ A2600 2.6 r.v. Compounding Grade Nylon 6, Dry As Molded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Neat resin, for compounding.Information provided by Cresset Powers Ltd.
Physical Properties Metric English Comments
Density 1.12 - 1.14 g/cc
0.0405 - 0.0412 lb/in³
ASTM D792
Apparent Bulk Density >= 0.659 g/cc
>= 0.0238 lb/in³
Viscosity Measurement 2.6
2.6
Relative Viscosity
Melt Flow 14 - 20 g/10 min

@Load 2.16 kg,
Temperature 230 °C
 14 - 20 g/10 min

@Load 4.76 lb,
Temperature 446 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield >= 65.0 MPa
>= 9430 psi
ASTM D638
Elongation at Yield <= 6.0 %
<= 6.0 %
ASTM D638
Flexural Yield Strength >= 85.0 MPa
>= 12300 psi
ASTM D790
Flexural Modulus >= 2.50 GPa
>= 363 ksi
ASTM D790
Izod Impact, Notched >= 0.240 J/cm
>= 0.450 ft-lb/in
ASTM D256, Notch
Thermal Properties Metric English Comments
Melting Point 220 - 224 °C
428 - 435 °F
ASTM DSC
Deflection Temperature at 1.8 MPa (264 psi) >= 55.0 °C
>= 131 °F
Processing Properties Metric English Comments
Moisture Content <= 0.080 %
<= 0.080 %
Descriptive Properties Value Comments
Extractables, wt% <0.4