- Fiberfil® PP-61/TC/20 Polypropylene Copolymer, 20% Talc
Fiberfil® PP-61/TC/20 Polypropylene Copolymer, 20% Talc
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | FiberFil |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Fiberfil® PP-61/TC/20 Polypropylene Copolymer, 20% Talc.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by FIBERFIL Engineered Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Water Absorption | 0.020 % | 0.020 % | 24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.010 cm/cm @Thickness 3.17 mm |
0.010 in/in @Thickness 0.125 in |
ASTM D955 |
| 0.012 cm/cm @Thickness 6.35 mm |
0.012 in/in @Thickness 0.250 in |
ASTM D955 | |
| Melt Flow | 15 - 20 g/10 min | 15 - 20 g/10 min | 230/2.16 (typical); ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 80 - 90 | 80 - 90 | ASTM D785 |
| Tensile Strength, Yield | 23.4 MPa | 3400 psi | ASTM D638 |
| Elongation at Yield | 25 % | 25 % | ASTM D638 |
| Tensile Modulus | 1.90 GPa | 275 ksi | ASTM D638 |
| Flexural Strength | 33.8 MPa | 4900 psi | ASTM D790 |
| Flexural Modulus | 1.70 GPa | 246 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 0.961 J/cm @Thickness 3.17 mm |
1.80 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 73.9 °C | 165 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.6 °C | 150 °F | ASTM D648 |
Users viewing this material also viewed the following:
- NatureWorks® Ingeo™ 7032D Stretch Blow Molding/Bottle Grade PLA
- SABIC Innovative Plastics Lexan® FST9705 PC Copolymer
- S&E Specialty Polymers TufTech™ GM-3968 PVC Compound
- SABIC Innovative Plastics Lexan® HFD1830 PC Copolymer (Europe-Africa-Middle East)
- Albis Plastics Cellulose Acetate Propionate CP800 (Base Grade), 8% Plasticizer (discontinued **)
- Gromax CCP ABS/PBT 7320H-104 20% Glass Fiber Filled
- Borealis Borclear™ RE936CF Polypropylene Random Copolymer
- Goodfellow Cobalt/Silicon/Boron/Manganese Alloy
- Cossa Polimeri ESTALUX 9202 A Methyl Methacrylate Acrylonitrile Butadiene Styrene
- 3M 9415PC Repositionable Tape
Copyright © lookpolymers.com All Rights Reserved