Samyang Triel® 5650 Thermoplastics Polyetherester Elastomer, General Extrusion
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyester, TP , Polyether Ester Elastomer |
| Manufacturer | Samyang |
| Trade Name | Triel® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samyang Triel® 5650 Thermoplastics Polyetherester Elastomer, General Extrusion.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Excellent mechanical characteristics, elasticity, thermal resistance and chemical resistance.5650 is an extrusion grade.Information provided by Samyang.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | ASTM D792 |
| Water Absorption | 0.50 % | 0.50 % | ASTM D570 |
| Linear Mold Shrinkage | 0.017 - 0.020 cm/cm | 0.017 - 0.020 in/in | ASTM D955 |
| Melt Flow | 10 g/10 min @Load 2.16 kg, Temperature 230 °C |
10 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| 10 g/10 min @Load 2.16 kg, Temperature 240 °C |
10 g/10 min @Load 4.76 lb, Temperature 464 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 65 | 65 | ASTM D2240 |
| Tensile Strength, Ultimate | 34.3 MPa | 4980 psi | ASTM D638 |
| Tensile Strength, Yield | 18.6 MPa @Strain 5.00 % |
2700 psi @Strain 5.00 % |
ASTM D638 |
| 23.0 MPa @Strain 10.0 % |
3340 psi @Strain 10.0 % |
ASTM D638 | |
| 23.5 MPa @Strain 50.0 % |
3410 psi @Strain 50.0 % |
ASTM D638 | |
| Flexural Yield Strength | 16.2 MPa | 2350 psi | ASTM D790 |
| Flexural Modulus | 0.358 GPa | 51.9 ksi | ASTM D790 |
| Izod Impact, Notched | 0.883 - 1.08 J/cm @Thickness 3.17 mm, Temperature -40.0 °C |
1.65 - 2.02 ft-lb/in @Thickness 0.125 in, Temperature -40.0 °F |
ASTM D256 |
| NB @Thickness 3.17 mm, Temperature 23.0 °C |
NB @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 208 °C | 406 °F | ASTM D2117 |
| Deflection Temperature at 0.46 MPa (66 psi) | 117 °C | 243 °F | ASTM D648 |
| Vicat Softening Point | 200 °C | 392 °F | ASTM D1525 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Flexible Rate | > 400% | ASTM D638 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® CFR5630D PC COPOLYMER
- Lehmann & Voss LUVOCOM® 20-0951 Polyphthalamide, with carbon fiber
- Gromax BTQ50-DQ00N1 Nylon 6, Impact Modified (Conditioned)
- SABIC Innovative Plastics LNP THERMOCOMP AB002 ABS (Asia Pacific)
- Teijin Panlite® LN-1010RM High Light Reflection, Flame Resistant Polycarbonate Resin
- A. Schulman POLYBATCH™ Bright White P80514PF Concentrate Based In Polypropylene
- Diamond Polymers ASA S710
- 3M 12054 Black 1/4" (6.4 mm) Polyurethane Foam
- SABIC Innovative Plastics LNP Verton RX93407D PA 66 (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved