Asahi Kasei Tenac® 7054 Homopolymer Acetal Resin
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Unreinforced |
| Manufacturer | Asahi Kasei |
| Trade Name | Tenac® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Asahi Kasei Tenac® 7054 Homopolymer Acetal Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High-flow grade with high crystallization rate for higher productivity.Information provided by Asahi Kasei Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.017 - 0.021 cm/cm | 0.017 - 0.021 in/in | Asahi Kasei Method |
| Melt Flow | 39 g/10 min | 39 g/10 min | ISO 1133 D |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 74.0 MPa | 10700 psi | ISO 527 - 1 & - 2 |
| Elongation at Break | 25 % | 25 % | ISO 527 - 1 & - 2 |
| Tensile Modulus | 3.40 GPa | 493 ksi | ISO 527 - 1 & - 2 |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179 / 1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ISO 75 -1 & -2 flat |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | ISO 75 -1 & -2 flat |
| Flammability, UL94 | HB | HB |
Users viewing this material also viewed the following:
- Polimeri Europa Europrene® 1500 Emulsion Styrene-Butadiene Rubber
- Multibase Multi-Flex® D 3604 TPE Thermoplastic Elastomer
- A. Schulman POLYBATCH™ Red 5670 Concentrate Based In Polyethylene
- Elektro-Isola G-Etronax PM GPO 3 Polyester, Glass Mat, Red, Sheets
- Eurostar Staramide AK8 PA66, 40% Mineral Reinforced, Injection Molding
- Aclo Accutech Polypropylene Copolymer CP0436W30L1 Wollastonite Reinforced
- Ascend Performance Materials VYDYNE® R533H Nylon, 33% Glass Reinforced, Conditioned
- ATI Allegheny Ludlum Martensitic Stainless Steel Type 425 Mod, Hardened + 204°C Temper
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 2.0 PHR Thanecure ZM
Copyright © lookpolymers.com All Rights Reserved